ALM PA-616-GS Filled Nylon 12 Prototyping Polymer
| Category | Polymer , Rapid Prototyping Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | ALM Advanced Laser Materials |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ALM PA-616-GS Filled Nylon 12 Prototyping Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
50% glass sphere filled material for improved dimensional stability, increased stiffness, and higher temperature applications when compared to unfilled PA.The PA 616-GS can be processed on any laser sintering platform, but has been specifically engineered for EOS platforms.PA 616-GS is slightly less recyclable when compared to PA 615-GS, but produces a smooth part surface finish.Information provided by Advanced Laser Materials (ALM).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.750 g/cc | 0.0271 lb/in³ | ASTM D1895 |
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D792 |
| Particle Size | 50 µm | 50 µm | D50 |
| 35 - 100 µm | 35 - 100 µm | D10-D90 | |
| Melt Flow | 35 - 45 g/10 min @Load 5.00 kg, Temperature 235 °C |
35 - 45 g/10 min @Load 11.0 lb, Temperature 455 °F |
3 min; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | XY; ASTM D638 |
| Elongation at Break | 1.4 % | 1.4 % | XY; ASTM D638 |
| Tensile Modulus | 4.10 GPa | 595 ksi | XY; ASTM D638 |
| Flexural Modulus | 3.10 GPa | 450 ksi | XY; ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 186 °C | 367 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | 50% RH, 500V; ASTM D257 |
| Surface Resistance | 2.30e+14 ohm | 2.30e+14 ohm | 50% RH, 500V; ASTM D257 |
| Dielectric Constant | 3.7 | 3.7 | ASTM D150 |