API Megol AM DP2433/50PBT SEBS Adhesion Modified Overmolding for Polyesters

Category Polymer , Thermoplastic , Elastomer, TPE , Styrenic TPE
Manufacturer A.P.I. SpA
Trade Name Megol AM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF API Megol AM DP2433/50PBT SEBS Adhesion Modified Overmolding for Polyesters.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Over-molding allows for the creation of composite finished products in a single phase, removing the need for successive gluing or mechanical fixing steps. This also reduces environmental impact as there are no VOC emissions from adhesives and, as the components are not made from a range of incompatible materials, they are more easily recycled at the end of their useful life. The over-molding process can be used in highly technical applications such as components for the automotive industry, shells and casings for power tools, parts for domestic appliances, and seals which can be molded directly onto the frame.Information provided by A.P.I. SpA
Physical Properties Metric English Comments
Density 0.960 g/cc
0.0347 lb/in³
ASTM D 792
Mechanical Properties Metric English Comments
Hardness, Shore A 50

@Time 15.0 sec
50

@Time 0.00417 hour
ASTM D 2240
Tensile Strength 4.30 MPa
624 psi
ASTM D 638
Elongation at Break 600 %
600 %
ASTM D 638
100% Modulus 0.00180 GPa
0.261 ksi
ASTM D 638
300% Modulus 0.00300 GPa
0.435 ksi
ASTM D 638
Tear Strength 24.0 kN/m
137 pli
ASTM D 624
Compression Set 19 %

@Temperature 23.0 °C,
Time 259000 sec
19 %

@Temperature 73.4 °F,
Time 72.0 hour
ASTM D 395
47 %

@Temperature 70.0 °C,
Time 86400 sec
47 %

@Temperature 158 °F,
Time 24.0 hour
ASTM D 395
64 %

@Temperature 100 °C,
Time 86400 sec
64 %

@Temperature 212 °F,
Time 24.0 hour
ASTM D 395
Descriptive Properties Value Comments
Compatibility PBT
PC
PET
Food contact No
Hygroscopicity Slightly
Main Features Good Compression-set
Ozone Aging Resistance Excellent
72h, 40°C, 200 ppcm, Tension = 20%
Processing Injection Molding