Aardvark Polymers Aarlon® 2000 Rotational Molding Resin, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer Gehrig & Associates
Trade Name Aarlon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Aardvark Polymers Aarlon® 2000 Rotational Molding Resin, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Aarlon® 2000 PA 6/6 is a high performance nylon for rotational molding applications. Aarlon® 2000 offers high heat capabilities with exceptional mechanical properties.Information provided by Gehrig & Associates
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ASTM D792
Water Absorption 1.2 %
1.2 %
Immersion 24h; ASTM D570
Moisture Absorption at Equilibrium 2.6 %
2.6 %
ISO 62
Water Absorption at Saturation 8.5 %
8.5 %
ASTM D570
Linear Mold Shrinkage 0.014 cm/cm

@Thickness 2.00 mm
 0.014 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm

@Thickness 2.00 mm
 0.014 in/in

@Thickness 0.0787 in
 ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 79
79
ASTM D785
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength, Ultimate 83.0 MPa
12000 psi
ASTM D638
Tensile Strength, Yield 82.0 MPa
11900 psi
ISO 527
83.0 MPa
12000 psi
ASTM D638
Elongation at Break 60 %
60 %
ASTM D638
Elongation at Yield 4.5 %
4.5 %
ISO 527
Tensile Modulus 3.70 GPa
537 ksi
ISO 527
Flexural Modulus 2.80 GPa
406 ksi
ISO 178
Shear Strength 66.2 MPa
9600 psi
ASTM D732
Izod Impact, Unnotched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
0.320 J/cm

@Temperature -40.0 °C
 0.599 ft-lb/in

@Temperature -40.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 5.50 kJ/m²
2.62 ft-lb/in²
ISO 180/1A
5.50 kJ/m²

@Temperature -40.0 °C
 2.62 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
Charpy Impact Unnotched 40.0 J/cm²
190 ft-lb/in²
Low Temp; ISO 179/1eU
Charpy Impact, Notched 0.550 J/cm²
2.62 ft-lb/in²
ISO 179/1eA
0.300 J/cm²

@Temperature -30.0 °C
 1.43 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1E
0.450 J/cm²

@Temperature -30.0 °C
 2.14 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1EA
Tensile Impact Strength 504 kJ/m²
240 ft-lb/in²
Long Specimen; ISO 179/1eA
1470 kJ/m²
699 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 100 µm/m-°C

@Temperature 23.0 - 55.0 °C
 55.6 µin/in-°F

@Temperature 73.4 - 131 °F
 ASTM E831
CTE, linear, Transverse to Flow 110 µm/m-°C

@Temperature 23.0 - 55.0 °C
 61.1 µin/in-°F

@Temperature 73.4 - 131 °F
 ASTM E831
Melting Point 262 °C
504 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
ISO 75-1/-2
210 °C
410 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ASTM D648
70.0 °C
158 °F
ISO 75-1/-2
Brittleness Temperature -80.0 °C
-112 °F
ASTM D746
UL RTI, Electrical 130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 UL 746B
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 1.50 mm
 167 °F

@Thickness 0.0591 in
 UL 746B
UL RTI, Mechanical without Impact 85.0 °C

@Thickness 1.50 mm
 185 °F

@Thickness 0.0591 in
 UL 746B
Flammability, UL94 V-2

@Thickness 0.710 mm
 V-2

@Thickness 0.0280 in
 IEC 60695-11-10
V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
Oxygen Index 28 %
28 %
ASTM D2863
Electrical Properties Metric English Comments
Dielectric Constant 3.6

@Frequency 100 Hz
 3.6

@Frequency 100 Hz
 ASTM D150
3.9

@Frequency 1000 Hz
 3.9

@Frequency 1000 Hz
 ASTM D150
4.0

@Frequency 1e+6 Hz
 4.0

@Frequency 1e+6 Hz
 ASTM D150
Dissipation Factor 0.010

@Frequency 100 Hz
 0.010

@Frequency 100 Hz
 ASTM D150
0.020

@Frequency 1000 Hz
 0.020

@Frequency 1000 Hz
 ASTM D150
0.020

@Frequency 1e+6 Hz
 0.020

@Frequency 1e+6 Hz
 ASTM D150