Abatron AboCast/AboCure 8110-1 Flexible Epoxy

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive, Flexible
Manufacturer Abatron
Trade Name AboCast/AboCure
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Abatron AboCast/AboCure 8110-1 Flexible Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This epoxy system can achieve flexibility and plasticity without sacrificing adhesive, electrical, structural, and other properties. This compound is a clear (unfilled) basic formulation. Its applications include: bonding, laminating, casting, embedding, electrical potting, impregnating, coating, etc. It can be supplied in several variations to modify viscosity, reaction rate, color, most physical and chemical properties, and with many fillers to meet most requirements.
Physical Properties Metric English Comments
Water Absorption 6.2 %

@Time 7200 sec
6.2 %

@Time 2.00 hour
boil; cured 2 hours @ 93°C
11.9 %

@Time 2.59e+6 sec
11.9 %

@Time 720 hour
immersion; cured 30 days @ 25°C
12.2 %

@Time 2.59e+6 sec
12.2 %

@Time 720 hour
immersion; cured 7 days @ 25°C
Viscosity 2570 cP
2570 cP
Mechanical Properties Metric English Comments
Hardness, Shore A 11

@Temperature 75.0 °C
11

@Temperature 167 °F
cured 7 days @ 25°C
21

@Temperature 25.0 °C
21

@Temperature 77.0 °F
cured 7 days @ 25°C
28

@Temperature 75.0 °C
28

@Temperature 167 °F
cured 30 days @ 25°C
38

@Temperature 75.0 °C
38

@Temperature 167 °F
cured 2 hrs. @ 93°C
40

@Temperature 25.0 °C
40

@Temperature 77.0 °F
cured 30 days @ 25°C
47

@Temperature 25.0 °C
47

@Temperature 77.0 °F
cured 2 hrs. @ 93°C
Hardness, Shore D 23

@Temperature 0.000 °C
23

@Temperature 32.0 °F
cured 7 days @ 25°C
23

@Temperature 0.000 °C
23

@Temperature 32.0 °F
cured 30 days @ 25°C
60

@Temperature 0.000 °C
60

@Temperature 32.0 °F
cured 2 hrs. @ 93°C
77

@Temperature -60.0 °C
77

@Temperature -76.0 °F
cured 30 days @ 25°C
82

@Temperature -60.0 °C
82

@Temperature -76.0 °F
cured 7 days @ 25°C
83

@Temperature -60.0 °C
83

@Temperature -76.0 °F
cured 2 hrs. @ 93°C
Tensile Strength, Ultimate 0.172 MPa
25.0 psi
cured 7 days @ 25°C
0.241 MPa
35.0 psi
cured 2 hours @ 93°C
0.345 MPa
50.0 psi
cured 30 days @ 25°C
0.758 MPa
110 psi
cured 8 hours @ 93°C
Elongation at Break 68 %
68 %
cured 8 hours @ 93°C
90 %
90 %
cured 30 days @ 25°C
160 %
160 %
cured 2 hours @ 93°C
180 %
180 %
cured 7 days @ 25°C
Shear Strength 3.59 MPa

@Temperature 75.0 °C
520 psi

@Temperature 167 °F
Tensile, Al/Al lap joint; cured 2 hours @ 93°C
4.90 MPa

@Temperature 25.0 °C
710 psi

@Temperature 77.0 °F
Tensile, Al/Al lap joint; cured 2 hours @ 93°C
13.3 MPa

@Temperature 0.000 °C
1930 psi

@Temperature 32.0 °F
Tensile, Al/Al lap joint; cured 2 hours @ 93°C
Electrical Properties Metric English Comments
Volume Resistivity 2.90e+7 ohm-cm

@Temperature 150 °C
2.90e+7 ohm-cm

@Temperature 302 °F
cured 2 hours @ 93°C
3.00e+7 ohm-cm

@Temperature 100 °C
3.00e+7 ohm-cm

@Temperature 212 °F
cured 30 days @ 25°C
3.40e+7 ohm-cm

@Temperature 100 °C
3.40e+7 ohm-cm

@Temperature 212 °F
cured 2 hours @ 93°C
3.20e+8 ohm-cm

@Temperature 100 °C
3.20e+8 ohm-cm

@Temperature 212 °F
cured 7 days @ 25°C
6.60e+8 ohm-cm

@Temperature 25.0 °C
6.60e+8 ohm-cm

@Temperature 77.0 °F
cured 30 days @ 25°C
2.60e+9 ohm-cm

@Temperature 25.0 °C
2.60e+9 ohm-cm

@Temperature 77.0 °F
cured 2 hours @ 93°C
4.30e+9 ohm-cm

@Temperature 25.0 °C
4.30e+9 ohm-cm

@Temperature 77.0 °F
cured 7 days @ 25°C
Processing Properties Metric English Comments
Pot Life 120 min

@Temperature 25.0 °C
120 min

@Temperature 77.0 °F
200 g
Descriptive Properties Value Comments
Parts by Weight (pbw) 100
AboCast 8110-1
6
AboCure 8110-1