- Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
- Aclo Accutech ABS ABS834G10L Glass Reinforced
Aclo Accutech ABS ABS834G10L Glass Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech ABS ABS834G10L Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | MD; ASTM D955 |
| Melt Flow | 0.30 g/10 min | 0.30 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 88 | 88 | ASTM D785 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D638 |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 2.499 GPa | 362.5 ksi | ASTM D638 |
| Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm | 2.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.1 °C | 187 °F |
Users viewing this material also viewed the following:
- PolyOne Stat-Tech™ AS-08CF/000 UV FR V0 Acrylonitrile Butadiene Styrene (ABS)
- Plastcom SLOVASTER® B1 GF 15 FRX 5 PBT reinforced with 15% glass fibre, with flame retardant
- Pacific Sintered Materials F-244-S(HT) High Carbon Steel Powdered Metal
- Karina 4000/141-IE MBPP Green Color Concentrate
- Kuraray SEPTON® S8004 Thermoplastic Rubber
- Universal Wire Works 625 Nickel Alloy Welding Wire
- A. Schulman POLYFLAM™ FPP 1006 Talc Filled Homopolymer Polypropylene
- CPT C-Flex® R70-005 Opaque Biocompatible TPE
- 3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive
Copyright © lookpolymers.com All Rights Reserved