Aclo Accutech Polypropylene Copolymer CP0437W30L1 Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437W30L1 Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MD; ASTM D955 |
| Melt Flow | 18 g/10 min | 18 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 47 | 47 | ASTM D785 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ASTM D638 |
| Elongation at Break | 16 % | 16 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 1.900 GPa | 275.5 ksi | ASTM D638 |
| Flexural Strength | 20.0 MPa | 2900 psi | ASTM D790 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
| Izod Impact, Notched | 1.92 J/cm | 3.60 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 97.8 °C | 208 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F |
Users viewing this material also viewed the following:
- Nylene® PA6/6 Glass Filled 5105 HS Nylon 6/6
- SABIC Innovative Plastics Cycolac® S705 ABS (Europe-Africa-Middle East)
- DSM Akulon® K224-PG6U (Dry) 33% Glass Reinforced, Impact Modified Nylon 6 (North America) (discontinued **)&l
- H.C. Starck Amperit® 720.054 Blended Chromium Oxide-Aluminum Oxide-Titanium Oxide 80-17-3 (Cr2O3-Al2O3-TiO2)
- Techmer ES HiFill® PBT G/CF30 40% Glass Bead Filler
- PlastxWorld CEVIAN® B5526 30% GF PBT/ABS Alloy
- DuPont™ Nomex® 410 Paper, 12 mil Nominal Thickness
- Clariant Renol ABS3470 ABS, High Heat, Low Gloss
- Loctite® Prism® 4011 Cyanoacrylate Adhesive
Copyright © lookpolymers.com All Rights Reserved