- Styrene Acrylonitrile (SAN), Molded, Glass Reinforced
- Aclo Accutech SAN SAN930G10L Glass Reinforced
Aclo Accutech SAN SAN930G10L Glass Reinforced
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech SAN SAN930G10L Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 83.98 MPa | 12180 psi | ASTM D638 |
| Tensile Strength, Yield | 83.98 MPa | 12180 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 4.100 GPa | 594.6 ksi | ASTM D638 |
| Flexural Strength | 113.0 MPa | 16390 psi | ASTM D790 |
| Flexural Modulus | 5.40 GPa | 783 ksi | ASTM D790 |
| Izod Impact, Notched | 0.342 J/cm | 0.640 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F |
Users viewing this material also viewed the following:
- MetaFoam Copper Foam
- H.C. Starck Amperit® 290.3 Water Atomized Nickel-Aluminum 69-31 (NiAl)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 1.5 PHR Sulfur
- Lubrizol ESTALOC® 59104 Ester-Type, Reinforced Engineering Thermoplastic
- Arkema Group Orgalloy® RS 6620 Polyamide 6.6 Alloy 20% Glass Fiber reinforced
- Alliance N-40SH Neodymium Iron Boron Magnetic Material
- 3D Systems Accura® SI 40 Plastic for the SLA® 500 System
- A. Schulman POLYBATCH™ Yellow 2214E Concentrate Based In Polyethylene
- DuPont Performance Polymers VTR 8505 Peroxide Cured Fluoroelastomer (FKM) Formulation (discontinued **)
Copyright © lookpolymers.com All Rights Reserved