Advanced Elastomer Systems VistaFlex® 912-B Thermoplastic Rubber (discontinued **)

Category	Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Advanced Elastomer Systems VistaFlex® 912-B Thermoplastic Rubber (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: A black super high-flow thermoplastic elastomer especially designed for injection molding applications. It replaces soft thermoplastics such as SBS, SEBS, and PVC blends. Supplied as free-flowing pellets in 25 kilogram (55 pound) moisture barrier bags.Features: High flowGood surface appearance on molded partsGood tensile propertiesGood tear strengthProduct Notes: Values are for injection molded plaques, side gated.82.6 mm x 117.5 mm x 3 mmInformation provided by Advanced Elastomer Systems.Advanced Elastomer Systems is now a part of ExxonMobil. This grade was removed from the Advanced Elastomers Systems standard product line before the ExxonMobil acquisiton.

Physical Properties	Metric	English	Comments
Density	0.950 g/cc	0.0343 lb/in³	ASTM D792
Melt Flow	45 g/10 min @Load 5.00 kg, Temperature 230 °C	45 g/10 min @Load 11.0 lb, Temperature 446 °F

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	35	35	5 seconds; ASTM D2240
Tensile Strength, Yield	6.00 MPa	870 psi	At 100% elongation, across flow; ASTM D412
	10.0 MPa	1450 psi	Across flow; ASTM D412
Tensile Modulus	0.340 GPa	49.3 ksi	1mm/min; DIN 53457
Flexural Modulus	0.270 GPa	39.2 ksi	1.7 mm/min; DIN 53457
Izod Impact, Notched	NB @Temperature -35.0 °C	NB @Temperature -31.0 °F	ISO 180A
Tear Strength	89.4 kN/m	510 pli	73°F; ASTM D624

Thermal Properties	Metric	English	Comments
Vicat Softening Point	82.0 °C	180 °F	Vicat A, 1 kg; DIN 53460/ISO 306
Brittleness Temperature	-40.0 °C	-40.0 °F	ASTM D746

Processing Properties	Metric	English	Comments
Processing Temperature	175 - 240 °C	347 - 464 °F
Mold Temperature	20.0 - 40.0 °C	68.0 - 104 °F