Advanced Polymer Alloys DuraGrip™ 6150 BK Melt Processable Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO)
Manufacturer APA - Advanced Polymer Alloys
Trade Name DuraGrip™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Advanced Polymer Alloys DuraGrip™ 6150 BK Melt Processable Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DuraGrip™ 6150BK is designed to be a special purpose Melt Processable Elastomer (MPE) that is easy to use in injection molding and extrusion processes. DGR 6150BK has an excellent soft touch feel and will Bond to Nylon, ABS, PC, PC/ABS. DuraGrip™ 6100 series is hygroscopic and requires drying prior to use.Information provided by Advanced Polymer Alloys
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D471; ISO 2781
Viscosity 327000 cP

@Shear Rate 300 1/s,
Temperature 190 °C
327000 cP

@Shear Rate 300 1/s,
Temperature 374 °F
ASTM D3835
Linear Mold Shrinkage 0.019 cm/cm
0.019 in/in
0.021 cm/cm
0.021 in/in
Linear Mold Shrinkage, Transverse 0.00 cm/cm
0.00 in/in
0.0040 cm/cm
0.0040 in/in
Mechanical Properties Metric English Comments
Hardness, Shore A 52
52
Time of 5 seconds; ASTM D2240; ISO 48
Tensile Strength, Ultimate 5.86 MPa
850 psi
ASTM D412; ISO 37
6.857 MPa
994.5 psi
After 7 days at 70°C; ASTM D412 ISO 37
8.6150 MPa
1249.5 psi
After 7 days at 100oC; ASTM D412 ISO 37
Elongation at Break 360 %
360 %
ASTM D412; ISO 37
381.6 %
381.6 %
After 7 days at 70°C; ASTM D412 ISO 37
417.6 %
417.6 %
After 7 days at 100°C; ASTM D412 ISO 37
Modulus of Elasticity 0.00170 GPa
0.247 ksi
After 7 days at 100°C; ASTM D412 ISO 37
0.00181 GPa
0.263 ksi
After 7 days at 70°C; ASTM D412 ISO 37
100% Modulus 0.00179 GPa
0.260 ksi
ASTM D412; ISO 37
Graves Tear Strength 25.6 kN/m

@Temperature 23.9 °C
146 pli

@Temperature 75.0 °F
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 144
144
Cs-17 Wheel, 1000 g Load; ASTM D3389
Compression Set 19 %
19 %
After 22 Hr at 75°F (24°C); ASTM D395; ISO 815
76 %

@Temperature 70.0 °C
76 %

@Temperature 158 °F
22 hrs.; ASTM D395; ISO 815
87 %

@Temperature 100 °C
87 %

@Temperature 212 °F
22 hrs.; ASTM D395; ISO 815
Tensile Set 3.4 %
3.4 %
100% Tension; ASTM D412
Thermal Properties Metric English Comments
Brittleness Temperature -67.8 °C
-90.0 °F
ASTM D746; ISO 812
Processing Properties Metric English Comments
Processing Temperature 227 °C
440 °F
Rear Barrel Temperature 204 - 221 °C
400 - 430 °F
Middle Barrel Temperature 216 - 227 °C
420 - 440 °F
Front Barrel Temperature 227 - 238 °C
440 - 460 °F
Nozzle Temperature 227 - 249 °C
440 - 480 °F
Melt Temperature 227 - 254 °C
440 - 490 °F
Mold Temperature 43.3 - 54.4 °C
110 - 130 °F
Injection Pressure 1.03 - 3.45 MPa
150 - 500 psi
Cycle Time - Injection 0.50 - 2.0 sec
0.50 - 2.0 sec
boost
Screw Speed 25 - 100 rpm
25 - 100 rpm
Cure Time 0.167 - 0.333 min
0.00278 - 0.00556 hour
Cooling Time
Descriptive Properties Value Comments
Fluid Resistance - Volume Change, % (ASTM D471) 1
After 7 Days in Water at 212°F (100°C)
16
After 7 Days in ASTM Oil No.1 at 212°F (100°C)
47
After 7 Days in ASTM Ref. Fuel No. B at 75°F (24°C)
95
After 7 Days in IRM 903 Oil No.3 at 212°F (100°C)