Akro-Plastic Akroloy® PA GF 30 (2718) PA 6.6 & PA6I/6T Dry, 30% Glass Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Akro-Plastic
Trade Name Akroloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Akro-Plastic Akroloy® PA GF 30 (2718) PA 6.6 & PA6I/6T Dry, 30% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important parameters. On the other side, there are important diminished design properties, such as rigidity, strength and creep modulus. It is also clear that the water molecules diffused into the polymer require a certain space, so that the dimensional stability suffers, as well. Applications that up to now have been manufactured of die-cast metals, usually involve extremely high demands on synthetic materials, running contrary to the above mentioned disadvantages. Even high levels of reinforcement in standard polyamides on the basis of PA 6 or PA 6.6 with, for example, 50 % or 60 % glass fibres, still exhibit drastic changes in mechanical characteristics. By blending of PA 6.6 with a partially aromatic CoPA (PA 6I/6T), it is possible to significantly reduce the influence of moisture on the product characteristics. While the drop in rigidity and strength of PA 6.6 GF 50 in a standard climate is still at approx. 25 %, a partially aromatic blend nevertheless exhibits a drop of less than 10 %. Furthermore, it becomes apparent that the toughness remains virtually unaffected. As a result of these findings, the swelling behaviour is improved, as well, which is favourable for dimensional stability. At the same time, this material mix also increases the glass transition temperature range. All in all, partly aromatic PA 6.6-Blends offer exactly the characteristics that are demanded by designers and users.Processing: AKROLOY® PA is based on a semi-crystalline PA 6.6 and an amorphous CoPA. This essentially determines the processing conditions. Accordingly, the melting point of AKROLOY® PA is at approx. 255 °C and is not influenced by the CoPA. With increasing temperatures, the amorphous contents provide a disproportionately low viscosity. The result is a very good reproduction of mould surfaces and a mass temperature that is up to 30 °C lower than required by comparable products. This results, aside from high quality surface finishes, frequently in reductions of cycle times, as well. Owing to production conditions, this must be verified in each individual case. Overall, AKROLOY® PA represents a step towards energy savings, in particular, when energy costs are compared to those in metal production and processing.Due to increasing cost pressure in many industrial sectors, AKROLOY® PA will become a very interesting alternative material in the area of substitutes for metal diecasting. Aside from already mentioned advantages in the service life of the mould, the omission of post processing allows an average cost reduction of up to 50 % – and more. The following list comprises imaginable and suitable areas of application, grouped by segments.Applications:Automotive Industry:Ignition key switch housingDoor handle componentsdoor lock componentsInstrument panels (centre console)Arm restsElectric motor housingsWiper componentsCarriers for wood decor stripsSeat sliding mechanisms, etc.Sanitary Installation:Single lever tapsWater filter housingsHousing for bath tapChrome-plated shower heads, levels, etc. Construction:Window locksDoor lock componentsExpanding nails for insulating plugsCorner connectors for lighting systemsShelving support elements, etc.Household:HandlesCoffee maker componentsJuice extractor componentsKnives and handlesBottle openersNutcrackers, etc. Electronic Industry:Mobile phone housingsPlastic tongsHousings for measuring unitsCarrier plates, etc. Machine Building:Plastic screwsCalipersScrew clamps, etc.Information from Akro-Plastic
Physical Properties Metric English Comments
Density 1.38 g/cc

@Temperature 23.0 °C
0.0499 lb/in³

@Temperature 73.4 °F
ISO 1183
Filler Content 30 %
30 %
ISO 1172
Water Absorption 1.55 %

@Temperature 70.0 °C
1.55 %

@Temperature 158 °F
62% r.h., Humidity; ISO 62
Water Absorption at Saturation 4.5 - 5.0 %
4.5 - 5.0 %
ISO 62
Linear Mold Shrinkage, Flow <= 0.0010 cm/cm
<= 0.0010 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ISO 294-4
Spiral Flow 757 cm
298 in
Akro
Mechanical Properties Metric English Comments
Ball Indentation Hardness 240 MPa
34800 psi
(H 961/30); ISO 2039-1
Tensile Strength at Break 210 MPa
30500 psi
5 [mm/min]; ISO 527-1/2
105 MPa

@Temperature 140 - 150 °C,
Time 1.80e+7 sec
15200 psi

@Temperature 284 - 302 °F,
Time 5000 hour
5 [mm/min], 50% Loss of Tensile Strength; ICE 216
105 MPa

@Temperature 140 - 150 °C,
Time 7.20e+7 sec
15200 psi

@Temperature 284 - 302 °F,
Time 20000 hour
5 [mm/min], 50% Loss of Tensile Strength; ICE 216
Elongation at Break 3.0 %
3.0 %
5 [mm/min]; ISO 527-1/2
4.0 %
4.0 %
Flexural Stain, 2.0mm/min; ISO 178
Tensile Modulus 10.5 GPa
1520 ksi
1[mm/min]; ISO 527-1/2
Flexural Strength 265 MPa
38400 psi
2 [mm/min]; ISO 178
Flexural Modulus 9.30 GPa
1350 ksi
2 [mm/min]; ISO 178
Charpy Impact Unnotched 6.50 J/cm²

@Temperature -30.0 °C
30.9 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
8.00 J/cm²

@Temperature 23.0 °C
38.1 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.10 J/cm²

@Temperature 23.0 °C
5.23 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
11.1 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/2
CTE, linear, Transverse to Flow 75.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
41.7 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/2
Melting Point 255 °C
491 °F
ISO 11357-1, DSC,10 [K/min]
Deflection Temperature at 0.46 MPa (66 psi) 245 °C
473 °F
HDT/B; ISO 75-1/2
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
HDT/A; ISO 75-1/2
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 80.0 °C
176 °F
Nozzle Temperature 290 - 310 °C
554 - 590 °F
Zone 1 275 - 305 °C
527 - 581 °F
Zone 2 275 - 305 °C
527 - 581 °F
Zone 3 275 - 305 °C
527 - 581 °F
Zone 4 275 - 305 °C
527 - 581 °F
Melt Temperature 290 - 310 °C
554 - 590 °F
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4 - 8 hour
4 - 8 hour
Injection Pressure 100 MPa
14500 psi
Hold Pressure 30.0 - 80.0 MPa
4350 - 11600 psi
Back Pressure 0.500 - 1.50 MPa
72.5 - 218 psi
Descriptive Properties Value Comments
Rate acc. FMVSS 302 ( Passed
Rate acc. FMVSS 302,( FMVSS 302, >1 [mm] Thickness