Akro-Plastic Akromid® B3 (2500) PA 6 Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Akro-Plastic
Trade Name Akromid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Akro-Plastic Akromid® B3 (2500) PA 6 Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatures as well as easy processing. AKROMID® B is an engineering plastic compound that allows a broad range of possible applications. On the basis of these standard types, we are able to develop individual compounds for special application needs.Information from Akro-Plastic
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 2.6 - 3.4 %

@Temperature 70.0 °C
2.6 - 3.4 %

@Temperature 158 °F
62% r.h., Humidity; ISO 62
Water Absorption at Saturation 9.0 - 10 %

@Time 82800 sec
9.0 - 10 %

@Time 23.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.011 cm/cm
0.011 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 45.0 MPa
6530 psi
50 [mm/min], Test Speed 50 [mm/min]; ISO 527-1/2
Elongation at Break >= 50 %
>= 50 %
50 [mm/min]; ISO 527-1/2
Tensile Modulus 1.20 GPa
174 ksi
1[mm/min]; ISO 527-1/2
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.60 J/cm²

@Temperature 23.0 °C
7.61 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
ISO 11357-1/3
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 ohm-cm
1.00e+10 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
IEC 60093