Akro-Plastic Akromid® B3 GF 15 (2469) PA 6 Dry, 15% Glass Filled

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer Akro-Plastic
Trade Name Akromid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Akro-Plastic Akromid® B3 GF 15 (2469) PA 6 Dry, 15% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatures as well as easy processing. AKROMID® B is an engineering plastic compound that allows a broad range of possible applications. On the basis of these standard types, we are able to develop individual compounds for special application needs.Information from Akro-Plastic
Physical Properties Metric English Comments
Density 1.23 g/cc

@Temperature 23.0 °C
0.0444 lb/in³

@Temperature 73.4 °F
ISO 1183
Filler Content 15 %
15 %
ISO 1172
Water Absorption 2.6 - 2.9 %

@Temperature 70.0 °C
2.6 - 2.9 %

@Temperature 158 °F
62% r.h., Humditiy; ISO 62
Water Absorption at Saturation 7.7 - 8.3 %

@Time 82800 sec
7.7 - 8.3 %

@Time 23.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ISO 294-4
Spiral Flow 87.0 cm
34.3 in
Cross Section: 7[mm]x3.5[mm]; AKRO
Mechanical Properties Metric English Comments
Ball Indentation Hardness 180 MPa
26100 psi
H 961/30; ISO 2039-1
Tensile Strength at Break 120 MPa
17400 psi
5 [mm/min]; ISO 527-1/2
60.0 MPa

@Temperature 160 - 175 °C,
Time 1.80e+7 sec
8700 psi

@Temperature 320 - 347 °F,
Time 5000 hour
5 [mm/min], 50% Loss of Tensile Strength; ICE 216
60.0 MPa

@Temperature 130 - 150 °C,
Time 7.20e+7 sec
8700 psi

@Temperature 266 - 302 °F,
Time 20000 hour
5 [mm/min], 50% Loss of Tensile Strength; ICE 216
Elongation at Break 3.0 %
3.0 %
5 [mm/min]; ISO 527-1/2
Tensile Modulus 6.10 GPa
885 ksi
1[mm/min]; ISO 527-1/2
Flexural Strength 180 MPa
26100 psi
2 [mm/min]; ISO 178
Flexural Modulus 5.20 GPa
754 ksi
2 [mm/min]; ISO 178
Charpy Impact Unnotched 4.30 J/cm²

@Temperature -30.0 °C
20.5 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
5.20 J/cm²

@Temperature 23.0 °C
24.7 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 23.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
12.8 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/2
CTE, linear, Transverse to Flow 96.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
53.3 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/2
Melting Point 220 °C
428 °F
ISO 11357-1/3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
HDT/B; ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
HDT/A; ISO 75-2
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 1.60 mm
1200 °F

@Thickness 0.0630 in
ICE 60695-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Comparative Tracking Index 600 V
600 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Nozzle Temperature 240 - 280 °C
464 - 536 °F
Zone 1 225 - 300 °C
437 - 572 °F
Zone 2 225 - 300 °C
437 - 572 °F
Zone 3 225 - 300 °C
437 - 572 °F
Zone 4 225 - 300 °C
437 - 572 °F
Melt Temperature 260 - 300 °C
500 - 572 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2.00 hour
2.00 hour
Hold Pressure 30.0 - 80.0 MPa
4350 - 11600 psi
Back Pressure 5.00 - 10.0 MPa
725 - 1450 psi
Descriptive Properties Value Comments
Rate acc. FMVSS 302 ( Passed
Rate acc. FMVSS 302,( FMVSS 302, >1 [mm] Thickness
Resistance to Oleic acid Pass
100% Conc. at 23°C
Resistance to Acetaldehyde Fail
40% Conc. at 23°C
Resistance to Acetic Acid Pass
20% Conc. at 23°C
Resistance to Acetone Pass
100% Conc. at 23°C
Resistance to Acetonitrile Pass
100% Conc. at 23°C
Resistance to Acrylonitrile Pass
100% Conc. at 23°C
Resistance to Allyl alcohol Fail
96% Conc. at 23°C
Resistance to Amyl alcohol Pass
100% Conc. at 23°C
Resistance to Aqueous Ammonia Pass
10% Conc. at 23°C
Resistance to Benzene Fail
100% Conc. at 40°C
Pass
100% Conc. at 23°C
Pass
100% Conc. at 23°C
Resistance to Biodiesel Pass
100% Conc. at 23°C
Resistance to Boric acid Fail
100% Conc. at 23°C
Pass
10% Conc. at 23°C
Resistance to Brake fluid (DOT 4) Fail
100% Conc. at 130°C
Pass
100% Conc. at 23°C
Resistance to Calcium chloride, alcoholic Fail
10% Conc. at 23°C
Resistance to Calcium chloride, aqueous Pass
10% Conc. at 23°C
Resistance to Carbonic acid Pass
100% Conc. at 60°C
Resistance to Caustic potash solution, aqueous Pass
50% Conc. at 23°C
Resistance to Chloracetic acid Fail
50% Conc. at 23°C
Resistance to Chlorine Fail
100% Conc. at 23°C
Resistance to Chlorine water Fail
100% Conc. at 23°C
Resistance to Chromic acid Fail
10% Conc. at 23°C
Resistance to Cyclohexane Pass
100% Conc. at 23°C
Resistance to Cyclohexanol Pass
100% Conc. at 23°C
Resistance to Dichloro-Acetic acid Fail
50% Conc. at 23°C
Resistance to Diesel fuel (DIN 51601) Pass
100% Conc. at 23°C
Resistance to Ethanol Pass
96% Conc. at 23°C
Resistance to Ethylene glycol/water Fail
50% Conc. at 120°C
Resistance to Formaldehyde, aqueous Pass
10% Conc. at 23°C
Resistance to Formic acid Fail
2% Conc. at 23°C
Resistance to Glycerin Pass
100% Conc. at 23°C
Resistance to Hydraulic oil H and HL (DIN 51524) Pass
100% Conc. at 100°C
Resistance to Hydrogen chloride, gas Fail
100% Conc. at 23°C
Resistance to Iso-octanol Pass
100% Conc. at 23°C
Resistance to Isopropanol Pass
100% Conc. at 23°C
Resistance to Methanol Pass
100% Conc. at 23°C
Resistance to Methylene chloride Fail
100% Conc. at 23°C
Resistance to Motor oil (SAE 10W-40) Pass
100% Conc. at 130°C
Pass
100% Conc. at 23°C
Resistance to Natural Gas Pass
100% Conc. at 23°C
Resistance to Nitric acid Fail
40% Conc. at 23°C
Resistance to Ozone Fail
100% Conc. at 23°C
Resistance to Phenol Fail
100% Conc. at 23°C
Resistance to Phosphoric acid Fail
30% Conc. at 23°C
Resistance to Potassium chloride, aqueous Pass
10% Conc. at 23°C
Resistance to Potassium permanganate, aqueous Fail
10% Conc. at 23°C
Resistance to Sodium chloride, aqueous Pass
10% Conc. at 23°C
Resistance to Sodium hydroxide solution, aqueous Pass
1% Conc. at 23°C
Resistance to Sodium hypochlorite, aqueous Fail
10% Conc. at 23°C
Resistance to Transmission oil (ATF m 1375.4) Pass
100% Conc. at 150°C
Resistance to Urea, aqueous Pass
20% Conc. at 23°C
Resistant to Carbon disulphide Pass
100% Conc. at 23°C
Resistant to Carbon tetrachloride Pass
100% Conc. at 23°C
Resistant to Citric acid Pass
10% Conc. at 23°C
Resistant to Ethyl acetate Pass
100% Conc. at 23°C
Resistant to Hydrochloric acid Fail
36% Conc. at 23°C
Resistant to Hydrogen peroxide Fail
23°C
Resistant to Seawater Pass
100% Conc. at 23°C
Resistant to Silicone fluid Pass
23°C
Resistant to Sulphuric acid Fail
96% Conc. at 23°C
Resistant to Super-grade petrol (DIN 51600) Pass
100% Conc. at 23°C
Resistant to Toluol Pass
100% Conc. at 23°C
Resistant to Water Pass
100% Conc. up to 50°C
Resistant to Xylol Pass
100% Conc. at 23°C
Resistant to Zinc chloride, aqueous Fail
50% Conc. at 23°C