Akro-Plastic Akromid® S3 GF15 1 (3223) PA 6.10 Dry, 15% Glass Filled

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced
Manufacturer Akro-Plastic
Trade Name Akromid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Akro-Plastic Akromid® S3 GF15 1 (3223) PA 6.10 Dry, 15% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw material used is sebacic acid, synthesized from castor oil which is obtained from the seeds of Ricinus communis, the castor oil plant. From a technical standpoint, AKROMID® S closes the gap between PA 6/PA 6.6 and PA 12. It is characterized by significantly lower moisture absorption compared to PA 6 and PA 6.6. At 23 °C and 50 % relative humidity, typical values for these product types are 3 % and 2.8 %, respectively. With a value of approximately 1.4 %, PA 6.10 absorbs just half as much moisture and can therefore be used as an engineering material in applications requiring a high dimensional consistency. Moreover, it exhibits excellent cold impact resistance. Other outstanding characteristics include very good chemical resistance due to the structure of the polymer and high hydrolysis resistance, although it can be processed like all common polyamides. The materials from the PA 6.10 product family are further characterized by exceptional dimensional stability, good surface resistance, good abrasion resistance and wear behaviour, and an improved carbon footprint. This is due to the fact that the plant-based raw materials have already removed CO2 from the environment during their growth phase. The product portfolio currently comprises one non reinforced variant and several reinforced variants with a glass-fibre content ranging from 15 % to 50 %. AKROMID® S is a bioplastic according to today’s standards. Unlike certain materials used in the packaging industry, however, the material is not biodegradable. The distinguishing feature of AKROMID® S is its reduced ecological footprint: The use of harmful CO2 per ton of polyamide produced from renewable resources is significantly lower compared to one ton produced from fossil-based resources, without affecting the product’s performance characteristics.Applications:Automotive SectorConnectors and housingsNon-return valvesPower steering-fluid reservoirsCorrugated tubing and fluid pipesMachine Construction and Tool-BuildingGearsDoor handles and fittingsOffice equipment, housings, functional parts, amongst othersConnectors and plugsPower toolsSports and LeisureComponents in high-end garden toolsBicycle accessoriesSail-boat accessoriesWinter sports accessoriesInformation from Akro-Plastic
Physical Properties Metric English Comments
Density 1.18 g/cc

@Temperature 23.0 °C
0.0426 lb/in³

@Temperature 73.4 °F
ISO 1183
Filler Content 15 %
15 %
ISO 1172
Water Absorption 1.5 %

@Temperature 70.0 °C
1.5 %

@Temperature 158 °F
62% r.h., Humidity; ISO 62
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ISO 294-4
Spiral Flow 45.0 cm
17.7 in
AKRO
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
5 [mm/min]; ISO 527-1/2
Elongation at Break 5.5 %
5.5 %
5 [mm/min]; ISO 527-1/2
Tensile Modulus 5.00 GPa
725 ksi
1[mm/min]; ISO 527-1/2
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -30.0 °C
28.6 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
7.50 J/cm²

@Temperature 23.0 °C
35.7 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.500 J/cm²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
ISO 11357-1, DSC,10 [K/min]
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
HDT/B; ISO 75-1/2
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
HDT/A; ISO 75-1/2
Deflection Temperature at 8.0 MPa 75.0 °C
167 °F
HDT/C; ISO 75-1/2
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Processing Properties Metric English Comments
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Nozzle Temperature 240 - 295 °C
464 - 563 °F
Zone 1 220 - 300 °C
428 - 572 °F
Zone 2 220 - 300 °C
428 - 572 °F
Zone 3 220 - 300 °C
428 - 572 °F
Zone 4 220 - 300 °C
428 - 572 °F
Melt Temperature 260 - 310 °C
500 - 590 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time <= 4 hour
<= 4 hour
Hold Pressure 30.0 - 80.0 MPa
4350 - 11600 psi
Back Pressure 5.00 - 15.0 MPa
725 - 2180 psi
Descriptive Properties Value Comments
Rate acc. FMVSS 302 ( Passed
Rate acc. FMVSS 302,( FMVSS 302, >1 [mm] Thickness