Aleris HOGAL 5558 Aluminum 5026 H14/H34

Category Metal , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer Aleris
Trade Name HOGAL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Aleris HOGAL 5558 Aluminum 5026 H14/H34.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
HOGAL 5558 is produced according to EN AW-5026.Information provided by Aleris.
Physical Properties Metric English Comments
Density 2.66 g/cc
0.0961 lb/in³
AA 5083
Mechanical Properties Metric English Comments
Hardness, Brinell 88

@Thickness 5.00 - 12.0 mm
88

@Thickness 0.197 - 0.472 in
Typical
52

@Thickness 5.00 mm,
Temperature 200 °C
52

@Thickness 0.197 in,
Temperature 392 °F
Calculated
64

@Thickness 5.00 mm,
Temperature 150 °C
64

@Thickness 0.197 in,
Temperature 302 °F
Calculated
84

@Thickness 5.00 mm,
Temperature 100 °C
84

@Thickness 0.197 in,
Temperature 212 °F
Calculated
87

@Thickness 5.00 mm,
Temperature 25.0 °C
87

@Thickness 0.197 in,
Temperature 77.0 °F
Tensile Strength, Ultimate >= 250 MPa
>= 36300 psi
Guaranteed Minimum L-T Direction
290 MPa

@Thickness 5.00 - 12.0 mm
42100 psi

@Thickness 0.197 - 0.472 in
Typical L-T Direction
170 MPa

@Thickness 5.00 mm,
Temperature 200 °C
24700 psi

@Thickness 0.197 in,
Temperature 392 °F
Typical L-T Direction
211 MPa

@Thickness 5.00 mm,
Temperature 150 °C
30600 psi

@Thickness 0.197 in,
Temperature 302 °F
Typical L-T Direction
279 MPa

@Thickness 5.00 mm,
Temperature 100 °C
40500 psi

@Thickness 0.197 in,
Temperature 212 °F
Typical L-T Direction
292 MPa

@Thickness 5.00 mm,
Temperature 25.0 °C
42400 psi

@Thickness 0.197 in,
Temperature 77.0 °F
Typical L-T Direction
Tensile Strength, Yield >= 200 MPa
>= 29000 psi
Guaranteed Minimum L-T Direction; 0.2% Offset
230 MPa

@Thickness 5.00 - 12.0 mm
33400 psi

@Thickness 0.197 - 0.472 in
Typical L-T Direction; 0.2% Offset
Elongation at Break >= 10 %
>= 10 %
Guaranteed Minimum L-T Direction, in 2 inches
14 %

@Thickness 5.00 - 12.0 mm
14 %

@Thickness 0.197 - 0.472 in
Typical L-T Direction, in 2 inches
Bend Radius, Minimum 3.5 t

@Thickness 5.00 mm
3.5 t

@Thickness 0.197 in
4.0 t

@Thickness 8.00 mm
4.0 t

@Thickness 0.315 in
Component Elements Properties Metric English Comments
Aluminum, Al 88.3 - 94.6 %
88.3 - 94.6 %
as balance
Chromium, Cr <= 0.30 %
<= 0.30 %
Copper, Cu 0.10 - 0.80 %
0.10 - 0.80 %
Iron, Fe 0.20 - 1.0 %
0.20 - 1.0 %
Magnesium, Mg 3.9 - 4.9 %
3.9 - 4.9 %
Manganese, Mn 0.60 - 1.8 %
0.60 - 1.8 %
Silicon, Si 0.55 - 1.4 %
0.55 - 1.4 %
Titanium, Ti <= 0.20 %
<= 0.20 %
Zinc, Zn <= 1.0 %
<= 1.0 %
Zirconium, Zr <= 0.30 %
<= 0.30 %