Amity Thermosets ATG 116 Phenolic Molding Organic and inorganic Filler, Compression Molded

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer Amity Thermosets
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Amity Thermosets ATG 116 Phenolic Molding Organic and inorganic Filler, Compression Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics:Medium mechanical strength Medium electrical insulationGeneral purposeColor- BlackMedium flow Applications: Electrical accessories & fittings ( medium quality ) Domestic appliance handles & knobsBottle caps Lamp casing, housings Connectors, etc.Information provided by Amity Thermosets Limited
Physical Properties Metric English Comments
Density 1.40 - 1.46 g/cc
0.0506 - 0.0527 lb/in³
Molding; IS 867-1963
Apparent Bulk Density 0.680 - 0.730 g/cc
0.0246 - 0.0264 lb/in³
IS 867-1963
Water Absorption 0.35 - 0.48 %
0.35 - 0.48 %
IS 13411-1993
Linear Mold Shrinkage 0.0074 - 0.0086 cm/cm
0.0074 - 0.0086 in/in
IS 13411-1992
Mechanical Properties Metric English Comments
Tensile Strength at Break 42.0 - 54.0 MPa
6090 - 7830 psi
5 mm/min.; IS 867-1963
Shear Strength 60.0 - 70.0 MPa
8700 - 10200 psi
IS 867-1963
Izod Impact, Notched 0.220 - 0.400 J/cm
0.412 - 0.749 ft-lb/in
IS 13411-1992
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 - 1.00e+11 ohm-cm
1.00e+10 - 1.00e+11 ohm-cm
IS 3396-1979
Surface Resistance 3.2e+9 - 1.0e+10 ohm
3.2e+9 - 1.0e+10 ohm
IS 3396-1979
Dielectric Strength 3.00 - 5.00 kV/mm

@Temperature 90.0 °C
76.2 - 127 kV/in

@Temperature 194 °F
IS 2584-1963
Processing Properties Metric English Comments
Mold Temperature 160 - 180 °C
320 - 356 °F
Injection Pressure 15.68 - 34.3 MPa
2274 - 4970 psi
Mold Pressure
Cure Time 0.333 - 0.417 min
0.00556 - 0.00694 hour
per mm
Shelf Life 12.0 Month
12.0 Month
10-25°C