Amity Thermosets ATO 1510 Phenolic Molding Glass fiber Filler, Compression Molded

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer Amity Thermosets
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Amity Thermosets ATO 1510 Phenolic Molding Glass fiber Filler, Compression Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics:Shock resistantElectrical low lossHigh mechanical strengthHeat stableHigh electrical insulationDimensional stabilityGood mechanical tension bearing strengthMedium copper adhesionColor-black, brownMedium flow Applications:Commutators Parts or components which ought to bear high mechanical, electrical & thermal tension , etc. Information provided by Amity Thermosets Limited
Physical Properties Metric English Comments
Density 1.70 - 1.82 g/cc
0.0614 - 0.0658 lb/in³
Molding; IS 867-1963
Apparent Bulk Density 0.550 - 0.710 g/cc
0.0199 - 0.0257 lb/in³
IS 867-1963
Water Absorption 0.10 - 0.20 %
0.10 - 0.20 %
IS 13411-1993
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm
0.0020 - 0.0030 in/in
IS 13411-1992
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 - 70.0 MPa
7980 - 10200 psi
5 mm/min.; IS 867-1963
Shear Strength 70.0 - 90.0 MPa
10200 - 13100 psi
2mm/min.; IS 867-1963
Izod Impact, Notched 0.500 - 0.650 J/cm
0.937 - 1.22 ft-lb/in
IS 13411-1992
Electrical Properties Metric English Comments
Volume Resistivity 3.2e+11 - 1.0e+12 ohm-cm
3.2e+11 - 1.0e+12 ohm-cm
IS 3396-1979
Surface Resistance 1.00e+11 - 3.16e+11 ohm
1.00e+11 - 3.16e+11 ohm
IS 3396-1979
Dielectric Strength 8.50 - 10.0 kV/mm

@Temperature 90.0 °C
216 - 254 kV/in

@Temperature 194 °F
IS 2584-1963
Comparative Tracking Index >= 150 V
>= 150 V
2824-1975
Processing Properties Metric English Comments
Mold Temperature 160 - 180 °C
320 - 356 °F
Injection Pressure 15.68 - 34.3 MPa
2274 - 4970 psi
Mold Pressure
Cure Time 0.917 - 1.33 min
0.0153 - 0.0222 hour
per mm
Shelf Life 12.0 Month
12.0 Month
10-25°C