Amity Thermosets ATR 126 Phenolic Molding Organic Filler, Injection Molded

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer Amity Thermosets
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Amity Thermosets ATR 126 Phenolic Molding Organic Filler, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics:Ammonia freeGood mouldabilityGood mechanical strengthGood electrical insulationGood surface finishMedium thermal stability Color-black, brownSoft flow Applications:Telecommunication equipment partsAutomotive electrical parts Moulding which remain in contact with metal partsElectric switchgear components ( eg. relay )Components exposed to warm atmosphere, etc. Information provided by Amity Thermosets Limited
Physical Properties Metric English Comments
Density 1.32 - 1.37 g/cc
0.0477 - 0.0495 lb/in³
Molding; IS 867-1963
Apparent Bulk Density 0.600 - 0.680 g/cc
0.0217 - 0.0246 lb/in³
IS 867-1963
Water Absorption 0.20 - 0.40 %
0.20 - 0.40 %
IS 13411-1993
Linear Mold Shrinkage 0.0075 - 0.0090 cm/cm
0.0075 - 0.0090 in/in
IS 13411-1992
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 - 55.0 MPa
6670 - 7980 psi
5 mm/min.; IS 867-1963
Shear Strength 66.0 - 75.0 MPa
9570 - 10900 psi
2mm/min.; IS 867-1963
Izod Impact, Notched 0.220 - 0.300 J/cm
0.412 - 0.562 ft-lb/in
IS 13411-1992
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 - 3.16e+11 ohm-cm
1.00e+11 - 3.16e+11 ohm-cm
IS 3396-1979
Surface Resistance 1.00e+10 - 3.16e+10 ohm
1.00e+10 - 3.16e+10 ohm
IS 3396-1979
Dielectric Strength 5.00 - 7.00 kV/mm

@Temperature 90.0 °C
127 - 178 kV/in

@Temperature 194 °F
IS 2584-1963
Processing Properties Metric English Comments
Rear Barrel Temperature 65.0 - 85.0 °C
149 - 185 °F
Front Barrel Temperature 85.0 - 95.0 °C
185 - 203 °F
Nozzle Temperature <= 105 °C
<= 221 °F
Mold Temperature 160 - 180 °C
320 - 356 °F
Injection Pressure 98.0 - 196 MPa
14200 - 28400 psi
Hold Pressure 58.8 MPa
8530 psi
Cure Time 0.200 - 0.333 min
0.00333 - 0.00556 hour
per mm
Shelf Life 1.50 Month
1.50 Month
27-30°C
4.00 Month
4.00 Month
below 20°C