Amity Thermosets ATS 1613-G Phenolic Molding Nylon and inorganic Filler, Compression Molded

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer Amity Thermosets
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Amity Thermosets ATS 1613-G Phenolic Molding Nylon and inorganic Filler, Compression Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics:High dielectric & mechanical strengthWeather resistant Good electric insulationLow water absorption Good mechanical tension bearing capacityColor-blackSoft/Medium flow Applications:Railway signaling equipment parts Kitchen equipment ( e.g. mixers, dishwashers ) parts Components which ought to have good electric insulation in spite of exposure to humid atmosphere, etc. Information provided by Amity Thermosets Limited
Physical Properties Metric English Comments
Density 1.45 - 1.55 g/cc
0.0524 - 0.0560 lb/in³
Molding; IS 867-1963
Apparent Bulk Density 0.700 - 0.750 g/cc
0.0253 - 0.0271 lb/in³
IS 867-1963
Water Absorption 0.12 - 0.18 %
0.12 - 0.18 %
IS 13411-1993
Linear Mold Shrinkage 0.0035 - 0.0055 cm/cm
0.0035 - 0.0055 in/in
IS 13411-1992
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 - 65.0 MPa
7980 - 9430 psi
5 mm/min.; IS 867-1963
Shear Strength 77.0 - 88.0 MPa
11200 - 12800 psi
2mm/min.; IS 867-1963
Izod Impact, Notched 0.250 - 0.400 J/cm
0.468 - 0.749 ft-lb/in
IS 13411-1992
Electrical Properties Metric English Comments
Volume Resistivity 3.2e+11 - 1.0e+12 ohm-cm
3.2e+11 - 1.0e+12 ohm-cm
IS 3396-1979
Surface Resistance 1.00e+11 - 3.16e+11 ohm
1.00e+11 - 3.16e+11 ohm
IS 3396-1979
Dielectric Strength 7.00 - 9.00 kV/mm

@Temperature 90.0 °C
178 - 229 kV/in

@Temperature 194 °F
IS 2584-1963
Processing Properties Metric English Comments
Mold Temperature 160 - 180 °C
320 - 356 °F
Injection Pressure 15.68 - 34.3 MPa
2274 - 4970 psi
Mold Pressure
Cure Time 0.833 - 1.33 min
0.0139 - 0.0222 hour
per mm
Shelf Life 12.0 Month
12.0 Month
10-25°C