- Aremco Ceramabond™ 632 High Temperature Ceramic Adhesive/Paste, Mica Filled
Aremco Ceramabond™ 632 High Temperature Ceramic Adhesive/Paste, Mica Filled
| Category | Ceramic , Oxide , Silicon Oxide |
| Manufacturer | Aremco |
| Trade Name | Ceramabond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Ceramabond™ 632 High Temperature Ceramic Adhesive/Paste, Mica Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: Dielectric, High Strength Bonding: Ceramic to Metal, Metal to Metal Principal Use: Heaters, Sensors
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 - 1.50 g/cc | 0.0524 - 0.0542 lb/in³ | |
| Volatile Organic Compounds (VOC) Content | 0.000 g/l | 0.000 g/l | |
| Viscosity | 10000 - 25000 cP | 10000 - 25000 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Impact Test | 2.71 J | 2.00 ft-lb | Torque Strength; curing at 1000°F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 8.46 µm/m-°C | 4.70 µin/in-°F | |
| Maximum Service Temperature, Air | 1260 °C | 2300 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 5.91 kV/mm | 150 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Application Temp |
| Cure Time | 120 min @Temperature 93.3 °C |
2.00 hour @Temperature 200 °F |
Step 1, preceeded by 1-4 hour air set |
| 120 min @Temperature 260 °C |
2.00 hour @Temperature 500 °F |
Step 2 | |
| Shelf Life | 6.00 Month @Temperature 4.44 - 32.2 °C |
6.00 Month @Temperature 40.0 - 90.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | Good | after curing at 700°F for 2 hours |
| Alkali Resistance | Good | after curing at 700°F for 2 hours |
| Color | Tan | |
| Moisture Resistance | Good | after curing at 700°F for 2 hours |
| Solvent | Water | |
| Thinner | 632-T |
Users viewing this material also viewed the following:
- Omni Plastics OmniLon™ 6/6 PA6/6 HSL Unfilled/ Impact Modified Nylon
- PolyOne Geon™ Vinyl Flexible 90252 Polyvinyl Chloride, Flexible (PVC, Flexible)
- LyondellBasell Hifaxâ„¢ ETA-4161UV Thermoplastic Olefin Resin
- DuPont Performance Polymers Crastin® S620F20 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)&l
- Daikin POLYFLON M-392 PTFE Molding Powder, Free Flow
- Arlon 51576XC015A 0.015" (0.381 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Sax Polymers SAXALEN PPC344G25 Polypropylene Copolymer, 25% Glass Filled
- A. Schulman POLYTROPE™ TPP 1024E-01 Olefinic Elastomer For Sheet Extrusion
- DuPont Bynel® 50E631 Adhesive Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved