- Aremco Glass-Coat™ SGC4000 High Temperature Specialty Coatings Silicone-Glass
Aremco Glass-Coat™ SGC4000 High Temperature Specialty Coatings Silicone-Glass
| Category | Ceramic , Glass , Other Engineering Material , Ceramic/Metallic Coating |
| Manufacturer | Aremco |
| Trade Name | Glass-Coat™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Glass-Coat™ SGC4000 High Temperature Specialty Coatings Silicone-Glass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Silicone-glass-ceramic, gray, low viscosity, scratch resistant coating for stainless steel to 900°F (482°C)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.59 g/cc | 1.59 g/cc | |
| Solids Content | 55.5 % | 55.5 % | by volume |
| 74 % | 74 % | by weight | |
| Volatile Organic Compounds (VOC) Content | 419 g/l | 419 g/l | |
| Viscosity | 40 - 80 cP | 40 - 80 cP | |
| Thickness | 25.4 microns | 1.00 mil | Dry Film |
| 67.1 microns | 2.64 mil | Wet Film | |
| Storage Temperature | 4.44 - 32.2 °C | 40.0 - 90.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 482 °C | 900 °F | Continuous |
| Flash Point | 36.0 °C | 96.8 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 39.4 kV/mm | 1000 kV/in | DC |
| 39.4 kV/mm | 1000 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 10.0 - 48.9 °C | 50.0 - 120 °F | Application Temperature |
| Cure Time | 15.0 min | 0.250 hour | Air Set prior to curing |
| 30.0 min @Temperature 93.3 °C |
0.500 hour @Temperature 200 °F |
0.25 hr at 480°F, 0.20 hr at 1000°F | |
| Shelf Life | 6.00 Month | 6.00 Month | 40 -90 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Light Grey | |
| Dry Film Coverage ft2/gal | 890 | at 1 mil |
| Thinner | Ethanol |