Arkema Group KYNAR® 710, 710 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding

Category Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer Arkema
Trade Name KYNAR®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group KYNAR® 710, 710 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics: Natural resin - translucent, off-white hemispheres. HDP indicates higher color stability. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, fire resistance, abrasion resistance; low-smoke emission; high purityApplications:Chemical processing – production, storage and transfer of corrosive fluidsElectronics – protective sheathing, plenum and wiring insulationSemi-conductor industryFood stuff and Healthcare industriesTransportation – fuel line and pipe, thermoformed body componentsListed properties are typical for 700 series.Information provided by Arkema Inc.
Physical Properties Metric English Comments
Specific Gravity 1.77 - 1.79 g/cc
1.77 - 1.79 g/cc
ASTM D792
Bulk Density 0.961 g/cc
0.0347 lb/in³
Water Absorption 0.010 - 0.030 %

@Time 86400 sec
0.010 - 0.030 %

@Time 24.0 hour
Immersion; ASTM D570
Viscosity 400000 - 800000 cP

@Shear Rate 100 1/s,
Temperature 232 °C
400000 - 800000 cP

@Shear Rate 100 1/s,
Temperature 450 °F
Melt Viscosity; ASTM D3835
Linear Mold Shrinkage, Flow 0.019 - 0.035 cm/cm

@Time 86400 sec
0.019 - 0.035 in/in

@Time 24.0 hour
Linear Mold Shrinkage, Transverse 0.016 - 0.030 cm/cm

@Time 86400 sec
0.016 - 0.030 in/in

@Time 24.0 hour
Melt Flow 19 - 35 g/10 min

@Load 3.80 kg,
Temperature 232 °C
19 - 35 g/10 min

@Load 8.38 lb,
Temperature 450 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 75 - 80
75 - 80
ASTM D2240
Tensile Strength at Break 34.0 - 55.0 MPa
4930 - 7980 psi
ASTM D638
Tensile Strength 26.0 MPa

@Strain 20.0 %,
Temperature 100 °C
3770 psi

@Strain 20.0 %,
Temperature 212 °F
31.0 MPa

@Strain 20.0 %,
Temperature 70.0 °C
4500 psi

@Strain 20.0 %,
Temperature 158 °F
39.0 MPa

@Strain 20.0 %,
Temperature 50.0 °C
5660 psi

@Strain 20.0 %,
Temperature 122 °F
53.0 MPa

@Strain 20.0 %,
Temperature 23.0 °C
7690 psi

@Strain 20.0 %,
Temperature 73.4 °F
Tensile Strength, Yield 45.0 - 55.0 MPa
6530 - 7980 psi
ASTM D638
Elongation at Break 50 - 200 %
50 - 200 %
ASTM D638
Elongation at Yield 5.0 - 10 %
5.0 - 10 %
ASTM D638
Creep Strength 3.70 MPa

@Temperature 90.0 °C,
Time 360000 sec
537 psi

@Temperature 194 °F,
Time 100 hour
Deflection = 3.3%; Flexural Creep
3.70 MPa

@Temperature 90.0 °C,
Time 3.60e+6 sec
537 psi

@Temperature 194 °F,
Time 1000 hour
Deflection = 3.4%; Flexural Creep
3.70 MPa

@Temperature 60.0 °C,
Time 360000 sec
537 psi

@Temperature 140 °F,
Time 100 hour
Deflection = 1.5%; Flexural Creep
3.70 MPa

@Temperature 60.0 °C,
Time 3.60e+6 sec
537 psi

@Temperature 140 °F,
Time 1000 hour
Deflection = 1.7%; Flexural Creep
Tensile Modulus 0.900 GPa

@Temperature 100 °C
131 ksi

@Temperature 212 °F
1.00 GPa

@Temperature 70.0 °C
145 ksi

@Temperature 158 °F
1.40 GPa

@Temperature 50.0 °C
203 ksi

@Temperature 122 °F
1.379 - 2.31 GPa

@Temperature 23.0 °C
200.0 - 335 ksi

@Temperature 73.4 °F
ASTM D638
Flexural Strength 58.0 - 76.0 MPa

@Strain 5.00 %
8410 - 11000 psi

@Strain 5.00 %
ASTM D790
Flexural Modulus 1.655 - 2.31 GPa
240.0 - 335 ksi
ASTM D790
Compressive Strength 69.0 - 103 MPa
10000 - 14900 psi
ASTM D695
Izod Impact, Notched 1.07 - 2.14 J/cm
2.00 - 4.00 ft-lb/in
ASTM D256
Izod Impact, Unnotched 10.7 - 42.7 J/cm
20.0 - 80.0 ft-lb/in
ASTM D256
Coefficient of Friction, Dynamic 0.14
0.14
vs. steel; ASTM D1894
Coefficient of Friction, Static 0.20
0.20
vs. steel; ASTM D1894
Taber Abrasion, mg/1000 Cycles 5.0 - 9.0
5.0 - 9.0
1000 g pad; CS-17
Thermal Properties Metric English Comments
CTE, linear 89.0 µm/m-°C

@Temperature -40.0 °C
49.4 µin/in-°F

@Temperature -40.0 °F
122 µm/m-°C

@Temperature 0.000 °C
67.8 µin/in-°F

@Temperature 32.0 °F
119 - 144 µm/m-°C

@Temperature 22.8 °C
66.0 - 80.0 µin/in-°F

@Temperature 73.0 °F
ASTM D696
183 µm/m-°C

@Temperature 70.0 °C
102 µin/in-°F

@Temperature 158 °F
204 µm/m-°C

@Temperature 85.0 °C
113 µin/in-°F

@Temperature 185 °F
Specific Heat Capacity 1.17 - 1.51 J/g-°C
0.280 - 0.360 BTU/lb-°F
DSC
Thermal Conductivity 0.170 - 0.190 W/m-K
1.18 - 1.32 BTU-in/hr-ft²-°F
ASTM D433
Melting Point 165 - 172 °C
329 - 342 °F
Deflection Temperature at 0.46 MPa (66 psi) 125 - 140 °C
257 - 284 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 105 - 115 °C
221 - 239 °F
ASTM D648
Glass Transition Temp, Tg -40.0 - -38.0 °C

@Frequency 1.00 Hz
-40.0 - -36.4 °F

@Frequency 1.00 Hz
DMA
Decomposition Temperature 375 °C
707 °F
1% wt loss / in air; TGA
410 °C
770 °F
1% wt loss / in nitrogen; TGA
Flammability, UL94 V-0
V-0
Oxygen Index 44 %
44 %
ASTM D2868
60 %
60 %
select grades; ASTM D2868
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+14 ohm-cm

@Temperature 20.0 °C
2.00e+14 ohm-cm

@Temperature 68.0 °F
65% RH; ASTM D257
Dielectric Constant 4.5

@Frequency 1.00e+8 Hz
4.5

@Frequency 1.00e+8 Hz
ASTM D150
9.5

@Frequency 100 Hz
9.5

@Frequency 100 Hz
ASTM D150
Dielectric Strength 66.9 kV/mm
1700 kV/in
ASTM D149
Dissipation Factor 0.010 - 0.21

@Frequency 100 Hz
0.010 - 0.21

@Frequency 100 Hz
ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
195 - 220 °C
383 - 428 °F
Tube Extrusion
Middle Barrel Temperature 200 - 220 °C
392 - 428 °F
Injection Molding
210 - 240 °C
410 - 464 °F
Tube Extrusion
Front Barrel Temperature 200 - 240 °C
392 - 464 °F
Injection Molding
210 - 240 °C
410 - 464 °F
Tube Extrusion
Nozzle Temperature 200 - 240 °C
392 - 464 °F
Injection Molding