- Arkema Group Kynar® 6000 HDC N 119 PVDF (discontinued **)
Arkema Group Kynar® 6000 HDC N 119 PVDF (discontinued **)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Kynar® 6000 HDC N 119 PVDF
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designation ISO 12086-PVDF-E,GG1Z,Q.6E5.J.A.I.D, CD,Kynar PVDF are fluorinated thermoplastic homopolymers.Outstanding characteristics of Kynar: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermomechanical properties.Main applications of Kynar: corrosion protection in the chemical industry, coating (painting, coextrusion), off shore, wire and cable.Kynar 6000 HDC N 119 is a filled grade of granules with improved conductivity to eliminate electrostatic charges. To be used in extrusion and injection molding.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in³ | |
| Water Absorption | 0.020 % | 0.020 % | |
| Moisture Absorption at Equilibrium | 0.015 % | 0.015 % | Humidity Absorption |
| Melt Flow | 2.6 g/10 min @Load 5.00 kg, Temperature 230 °C |
2.6 g/10 min @Load 11.0 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min |
| Elongation at Break | 8.0 % | 8.0 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 171 °C | 340 °F | 10°C/min |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | |
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | 10°C/min |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 10000 ohm-cm | 10000 ohm-cm | |
| Surface Resistance | 10000 ohm | 10000 ohm | |
| Dissipation Factor | 0.071 @Frequency 100 Hz |
0.071 @Frequency 100 Hz |
|
| 0.37 @Frequency 1e+6 Hz |
0.37 @Frequency 1e+6 Hz |