Arkema Group LOTADER® 3410 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride

Category Polymer , Thermoplastic , EMAAA Terpolymer
Manufacturer Arkema
Trade Name LOTADER®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group LOTADER® 3410 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LOTADER 3410 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized by high-pressure autoclave process. LOTADER 3410 is a versatile adhesive for extrusion coating or lamination, designed as: Concentrate to be used in dry blend with LDPE. LOTADER 3410 improves adhesion of LDPE on alu foils, metallized or primerized films and some plastic films. Ready for use resin to be used pure. LOTADER 3410 gives excellent adhesion on substrates like alu foil, metallized plastics, paper, board, PE and many plastic films.Coextrusion tie layer for PE/PA and PE/EVOH in extrusion coating process.Information provided by Arkema Group
Physical Properties Metric English Comments
Density 0.940 g/cc

@Temperature 23.0 °C
0.0340 lb/in³

@Temperature 73.4 °F
ISO 1183
Butyl Acrylate Content 17 %
17 %
IRTF (internal)
Melt Index of Compound 5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 37
37
ASTM D2240
Tensile Strength at Break 8.00 MPa
1160 psi
ASTM D638
Elongation at Break 700 %
700 %
ASTM D638
Flexural Modulus 0.0600 GPa
8.70 ksi
ASTM D638
Thermal Properties Metric English Comments
Melting Point 89.0 °C
192 °F
DSC
Vicat Softening Point 47.0 °C

@Load 0.999 kg
117 °F

@Load 2.20 lb
ASTM D1525
Brittleness Temperature <= -50.0 °C
<= -58.0 °F
ASTM D726
Processing Properties Metric English Comments
Processing Temperature 270 - 330 °C
518 - 626 °F
Descriptive Properties Value Comments
Maleic Anhydride Content (%) 3.1
IRTF (internal)