Arkema Group Orgalloy® LT 5050ES Flexible Nylon Alloy (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon, Flexible Alloy
Manufacturer Arkema
Trade Name Orgalloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Orgalloy® LT 5050ES Flexible Nylon Alloy (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Very flexible polyamide alloy: easy to process, low moisture absorption, good mechanical properties at low temperature. Demonstrate a good balance of properties eg, high flexibility (500 MPa), good thermal performance and ductility at low temperatures.Suited to blow molding of technical parts under the hood (air intake). Sequential extrusion with RS or LE series (rigid flexible combinations). Blow molding of large parts.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
Melt Flow 1.0 g/10 min

@Load 5.00 kg,
Temperature 235 °C
1.0 g/10 min

@Load 11.0 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 23.0 MPa
3340 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal Strain; 50 mm/min
Elongation at Yield 10 %
10 %
50 mm/min
Tensile Modulus 0.460 GPa
66.7 ksi
1 mm/min
Tensile Creep Modulus, 1 hour 420 MPa
60900 psi
Tensile Creep Modulus, 1000 hours 270 MPa
39200 psi
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10°C/min
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Electrical Resistivity 7.40e+13 ohm-cm
7.40e+13 ohm-cm
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
Dielectric Constant 3.6

@Frequency 1e+6 Hz
3.6

@Frequency 1e+6 Hz
3.8

@Frequency 100 Hz
3.8

@Frequency 100 Hz
Dielectric Strength 36.0 kV/mm
914 kV/in
Dissipation Factor 0.050

@Frequency 1e+6 Hz
0.050

@Frequency 1e+6 Hz
0.11

@Frequency 100 Hz
0.11

@Frequency 100 Hz
Comparative Tracking Index 600 V
600 V