Arkema Group Orgalloy® R 6030 Nylon 6 Alloy, 30% Glass fiber (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Arkema
Trade Name Orgalloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Orgalloy® R 6030 Nylon 6 Alloy, 30% Glass fiber (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rigid polyamide 6 alloy: easy to process, low moisture absorption, chemical resistance (no known solvents).Special 30% glass fiber reinforced for overmolding with modified PP.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
Water Absorption 2.2 %
2.2 %
Moisture Absorption at Equilibrium 0.90 %
0.90 %
Humidity Absorption
Melt Flow 4.0 g/10 min

@Load 2.16 kg,
Temperature 235 °C
4.0 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 110 MPa
16000 psi
5 mm/min
Elongation at Break 2.9 %
2.9 %
5 mm/min
Tensile Modulus 7.20 GPa
1040 ksi
1 mm/min
Tensile Creep Modulus, 1 hour 5500 MPa
798000 psi
Tensile Creep Modulus, 1000 hours 3890 MPa
564000 psi
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10°C/min
Deflection Temperature at 0.46 MPa (66 psi) 212 °C
414 °F
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Oxygen Index 21 %
21 %
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
Dielectric Constant 2.6

@Frequency 100 Hz
2.6

@Frequency 100 Hz
3.4

@Frequency 1e+6 Hz
3.4

@Frequency 1e+6 Hz
Dielectric Strength 35.0 kV/mm
889 kV/in
Dissipation Factor 0.023

@Frequency 1e+6 Hz
0.023

@Frequency 1e+6 Hz
0.064

@Frequency 100 Hz
0.064

@Frequency 100 Hz
Comparative Tracking Index 600 V
600 V