Arkema Group Orgalloy® RS 6030 Polyamide 6 Alloy 30% Glass Fiber reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Arkema
Trade Name Orgalloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Orgalloy® RS 6030 Polyamide 6 Alloy 30% Glass Fiber reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide Alloy, Rigid grade, Nylon 6 basedMolding of Engineering PartsInformation provided by Arkema Group
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
ISO R1183
Water Absorption 0.60 %
0.60 %
23°C / 24 hrs; ISO 62
Moisture Absorption at Equilibrium 1.1 %
1.1 %
23°C / 50% RH; ISO 62
2.3 %
2.3 %
in 23°C water; ISO 62
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 235 °C
 3.0 g/10 min

@Load 4.76 lb,
Temperature 455 °F
 after drying; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 82
82
ISO 868
Tensile Strength, Ultimate 130 MPa
18900 psi
ISO R527
Elongation at Break 3.9 %
3.9 %
ISO R527
Modulus of Elasticity 7.50 GPa
1090 ksi
ISO R527
Flexural Strength 185 MPa
26800 psi
After conditioning at 23°C and 50% RH; ISO 178
204 MPa
29600 psi
Dry; ISO 178
Flexural Modulus 7.00 GPa
1020 ksi
After conditioning at 23°C and 50% RH; ISO 178
7.40 GPa
1070 ksi
Dry; ISO 178
Charpy Impact, Notched 2.20 J/cm²
10.5 ft-lb/in²
After conditioning at 23°C/50%RH; ISO 179/Af
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 Dry; ISO 179/Af
18.0 J/cm²

@Temperature -20.0 °C
 85.7 ft-lb/in²

@Temperature -4.00 °F
 Dry; ISO 179/Af
19.0 J/cm²

@Temperature -20.0 °C
 90.4 ft-lb/in²

@Temperature -4.00 °F
 After conditioning at 23°C/50%RH; ISO 179/Af
Tensile Creep Modulus, 1 hour 5740 MPa
833000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear 19.0 µm/m-°C

@Temperature 20.0 - 60.0 °C
 10.6 µin/in-°F

@Temperature 68.0 - 140 °F
 TMS2 Perkin Elmer
CTE, linear, Transverse to Flow 120 µm/m-°C

@Temperature 20.0 - 60.0 °C
 66.7 µin/in-°F

@Temperature 68.0 - 140 °F
 TMS2 Perkin Elmer
Melting Point 220 °C
428 °F
ISO R1218
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO R75
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
ISO R75
Vicat Softening Point 185 °C
365 °F
50 N - B method; ISO 306
>= 210 °C
>= 410 °F
10 N - A method; ISO 306
Flammability, UL94 HB
HB
Flame Spread 6.0 mm/min
0.24 in/min
FMVSS 302
Electrical Properties Metric English Comments
Volume Resistivity 1.30e+15 ohm-cm
1.30e+15 ohm-cm
ASTM D257
Surface Resistance 1.30e+15 ohm
1.30e+15 ohm
ASTM D257
Dielectric Strength 34.0 kV/mm

@Thickness 1.00 mm
 864 kV/in

@Thickness 0.0394 in
 ASTM D149
Dissipation Factor 0.023

@Frequency 100000 Hz
 0.023

@Frequency 100000 Hz
 NFC 26 230
0.064

@Frequency 100 Hz
 0.064

@Frequency 100 Hz
 NFC 26 230
0.066

@Frequency 1000 Hz
 0.066

@Frequency 1000 Hz
 NFC 26 230
Comparative Tracking Index >= 600 V
>= 600 V
NFC 26 220
Descriptive Properties Value Comments
Automotive classification D-3
FMVSS 302