Arkema Group Orgalloy® RS 6600 Nylon 66 Alloy, Rigid Grade (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Arkema
Trade Name Orgalloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Orgalloy® RS 6600 Nylon 66 Alloy, Rigid Grade (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RS 66 series, rigid polyamide 66 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties. Non-reinforced grade for injection molding.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
Water Absorption 2.9 %
2.9 %
Moisture Absorption at Equilibrium 1.2 %
1.2 %
Humidity Absorption
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 275 °C
15 g/10 min

@Load 4.76 lb,
Temperature 527 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 52.0 MPa
7540 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal Strain; 50 mm/min
Elongation at Yield 3.4 %
3.4 %
50 mm/min
Tensile Modulus 2.60 GPa
377 ksi
1 mm/min
Tensile Creep Modulus, 1 hour 2270 MPa
329000 psi
Tensile Creep Modulus, 1000 hours 980 MPa
142000 psi
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 65.0 µm/m-°C

@Temperature 20.0 °C
36.1 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 110 µm/m-°C

@Temperature 20.0 °C
61.1 µin/in-°F

@Temperature 68.0 °F
Melting Point 255 °C
491 °F
10°C/min
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
Dielectric Constant 1.9

@Frequency 100 Hz
1.9

@Frequency 100 Hz
3.0

@Frequency 1e+6 Hz
3.0

@Frequency 1e+6 Hz
Dielectric Strength 36.0 kV/mm
914 kV/in
Comparative Tracking Index 600 V
600 V