Arkema Group Orgalloy® RS 6620 Nylon 66 Alloy, 20% Glass Fiber (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer Arkema
Trade Name Orgalloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Orgalloy® RS 6620 Nylon 66 Alloy, 20% Glass Fiber (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RS 66 series, rigid polyamide 66 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties20 % glass filled, for injection molding and for extrusion of profiles.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Water Absorption 2.3 %
2.3 %
Moisture Absorption at Equilibrium 1.1 %
1.1 %
Humidity Absorption
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 275 °C
10 g/10 min

@Load 4.76 lb,
Temperature 527 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 110 MPa
16000 psi
5 mm/min
Elongation at Break 4.5 %
4.5 %
5 mm/min
Tensile Modulus 5.50 GPa
798 ksi
1 mm/min
Tensile Creep Modulus, 1 hour 4900 MPa
711000 psi
Tensile Creep Modulus, 1000 hours 3510 MPa
509000 psi
Thermal Properties Metric English Comments
Melting Point 255 °C
491 °F
10°C/min
Deflection Temperature at 0.46 MPa (66 psi) 240 °C
464 °F
Deflection Temperature at 1.8 MPa (264 psi) 220 °C
428 °F
Vicat Softening Point 160 °C
320 °F
50°C/hr; 50N
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
Dielectric Constant 2.6

@Frequency 100 Hz
2.6

@Frequency 100 Hz
3.5

@Frequency 1e+6 Hz
3.5

@Frequency 1e+6 Hz
Dielectric Strength 35.0 kV/mm
889 kV/in
Comparative Tracking Index 600 V
600 V