Arkema Group Rilsan® AESN Y T6L Nylon 12, MoS2 Filled (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer Arkema
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® AESN Y T6L Nylon 12, MoS2 Filled (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA12,EHLS,22-010,MD05Grade with molybdenum filler for extrusion. Available color: steel gray. Reinforced light and heat stabilizing agents.Low friction coefficient. No need of lubricant. Good impact strength. Easy to be processed.Example applications: Control cables tubing, parking brake control cable, cable for opening doors.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
Melt Flow 1.6 g/10 min

@Load 2.16 kg,
Temperature 235 °C
1.6 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 46.0 MPa
6670 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal Strain; 50 mm/min
Elongation at Yield 7.0 %
7.0 %
50 mm/min
Tensile Modulus 1.58 GPa
229 ksi
1 mm/min
Charpy Impact Unnotched NB
NB
NB
NB
Low Temp
Charpy Impact, Notched 0.680 J/cm²
3.24 ft-lb/in²
0.680 J/cm²

@Temperature -30.0 °C
3.24 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
Melting Point 174 °C
345 °F
(Dry)
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
Vicat Softening Point 143 °C
289 °F
50°C/hr; 50N
Flammability, UL94 V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
V-2

@Thickness 3.20 mm
V-2

@Thickness 0.126 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm