Arlon 25FR Low-Cost Ceramic Hydrocarbon

Category	Polymer , Thermoset
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 25FR Low-Cost Ceramic Hydrocarbon.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High Frequency, Low Loss Thermoset Laminate and Prepreg for Double-sided, Multilayer and Mixed Dielectric Printed Circuit BoardsLow loss ceramic-filled thermoset resinTight dielectric tolerance controlExcellent dimensional stabilityExcellent price/performance ratioBenefits:Greater signal integrityWider eye patternsExcellent dimensional stabilityUtilizes standard FR-4 processesExcellent thermal propertiesTypical Applications:Cellular Base Station Antennas, Power Amplifiers, Down ConvertersHigh Speed BackplanesThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.

Physical Properties	Metric	English	Comments
Density	1.80 g/cc	0.0650 lb/in³	ASTM D792 Method A
Water Absorption	0.090 %	0.090 %	IPC TM-650 2.6.2.1
Thickness	99.1 microns	3.90 mil	Prepreg thickness - glass style 1080
	147 microns	5.80 mil	Prepreg thickness - glass style 2112
	170 microns	6.70 mil	Prepreg thickness - glass style 2313
Outgassing - Total Mass Loss	0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C	0.00 % @Pressure <=1.93e-8 psi, Temperature 257 °F	Collected Volatiles; ASTM E595-90
	0.070 % @Pressure <=1.33e-10 MPa, Temperature 125 °C	0.070 % @Pressure <=1.93e-8 psi, Temperature 257 °F	Water Vapor Recovered; ASTM E595-90
	0.24 % @Pressure <=1.33e-10 MPa, Temperature 125 °C	0.24 % @Pressure <=1.93e-8 psi, Temperature 257 °F	ASTM E595-90

Mechanical Properties	Metric	English	Comments
Tensile Strength	96.5 MPa	14000 psi	ASTM D882
Flexural Strength	241.48 MPa	35024 psi	ASTM D790
Peel Strength	0.877 kN/m	5.00 pli	After Thermal Stress; IPC TM-650 2.4.8

Thermal Properties	Metric	English	Comments
CTE, linear	16.0 µm/m-°C	8.89 µin/in-°F	x, before Tg; IPC TM-650 2.4.24
	18.0 µm/m-°C	10.0 µin/in-°F	y, before Tg; IPC TM-650 2.4.24
CTE, linear, Transverse to Flow	59.0 µm/m-°C	32.8 µin/in-°F	z, before Tg; IPC TM-650 2.4.24
Thermal Conductivity	0.450 W/m-K @Temperature 100 °C	3.12 BTU-in/hr-ft²-°F @Temperature 212 °F	ASTM E1225
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Volume Resistivity	4.17e+14 ohm-cm	4.17e+14 ohm-cm	Condition A; IPC TM-650 2.5.17.1
Surface Resistance	8.90e+14 ohm	8.90e+14 ohm	Condition A; IPC TM-650 2.5.17.1
Dielectric Constant	3.58 @Frequency 1.00e+10 Hz	3.58 @Frequency 1.00e+10 Hz	C23/50; IPC TM-650 2.5.5.5
Dissipation Factor	0.0035 @Frequency 1.00e+10 Hz	0.0035 @Frequency 1.00e+10 Hz	C23/50; IPC TM-650 2.5.5.5

Descriptive Properties	Value	Comments
Temperature Coefficient of Dielectric (ppm/°C)	50	IPC TM-650 2.5.5.5 adapted (-10 - 140°C)