- Arlon 55578GA028 0.0280" Uncured/Cured Silicone Rubber with Fiberglass Substrate
Arlon 55578GA028 0.0280" Uncured/Cured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 55578GA028 0.0280" Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Interleave: LDPESide 2 Layer 2: Uncured Silicone RubberSide 2 Layer 1: Cured Silicone RubberSubstrate: Style 162 FiberglassSide 1: Cured Silicone RubberThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | Silicone Property; Arlon SQA-TMS-024 |
| Thickness | 38.1 microns | 1.50 mil | Side 1; Arlon SQA-TMS-003 |
| 50.8 microns | 2.00 mil | Side 2 Layer 1; Arlon SQA-TMS-003 | |
| 216 microns | 8.50 mil | Side 2 Layer 2; Arlon SQA-TMS-003 | |
| 406 microns | 16.0 mil | Substrate; Arlon SQA-TMS-003 | |
| 711 microns | 28.0 mil | Overall Thickness; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 44 | 44 | Silicone Property; Arlon SQA-TMS-014 |
| Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; Arlon SQA-TMS-008 |
| Elongation at Break | 650 % | 650 % | Silicone Property; Arlon SQA-TMS-008 |
| Peel Strength | 5.26 kN/m | 30.0 pli | Bond Strength (S2 to S2); Arlon SQA-TMS-011 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 18.3 kV/mm | 465 kV/in | Arlon SQA-TMS-020 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle | |
| Shelf Life | 6.00 Month @Temperature 21.1 °C |
6.00 Month @Temperature 70.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Green | Product |
| Naturally White | Substrate | |
| Total Product Weight (oz/yd2) | 23.4 | Arlon SQA-TMS-025 |