Arlon 55578XC028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 55578XC028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Side 1: Cured Silicone RubberSide 2: Cured/Uncured Layers This data Represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Thickness 12.7 microns
0.500 mil
Side 1, Skim Coat
50.8 microns
2.00 mil
Side 2, Cured
76.2 microns
3.00 mil
Polyethylene, Interleave
>= 203 microns
>= 8.00 mil
Side 2, Uncured
457 microns
18.0 mil
Prime Coated 162 Style Fiberglass, Substrate
686 - 787 microns
27.0 - 31.0 mil
Overall
Mechanical Properties Metric English Comments
Hardness, Shore A 40 - 50
40 - 50
Compound Property
Tensile Strength >= 5.52 MPa
>= 800 psi
Compound Property
Elongation at Break >= 500 %
>= 500 %
Compound Property
Peel Strength >= 1.05 kN/m
>= 6.00 pli
Bond Strength
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
UL RTI, Electrical 220 °C
428 °F
per UL card E54153
UL RTI, Mechanical without Impact 200 °C
392 °F
per UL card E54153
Flammability, UL94 HB
HB
Compound Rated
Electrical Properties Metric English Comments
Dielectric Strength >= 15.7 kV/mm
>= 400 kV/in
Processing Properties Metric English Comments
Cure Time 15.0 min

@Temperature 177 °C
0.250 hour

@Temperature 350 °F
Recommended Cure Cycle
120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Postcure Cycle
Shelf Life 6.00 Month
6.00 Month
From date of manufacture
Descriptive Properties Value Comments
Color Light Gray
Total Product Weight (oz/yd2) 28.4 - 31.4
Uncoated Fabric Break Strength 420 lb/in
Fill Direction, Substrate Property
700 lb/in
Warp Direction, Substrate Property
Copyright © lookpolymers.com All Rights Reserved