Arlon 75400R045 0.045" (1.14 mm) Uncured Silicone Rubber with Fiberglass Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 75400R045 0.045" (1.14 mm) Uncured Silicone Rubber with Fiberglass Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Side 1: Uncured Silicone RubberThis data Represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Thickness 76.2 microns
3.00 mil
Polyethylene , Interleave
330 microns
13.0 mil
7500 Fiberglass, Substrate
737 - 889 microns
29.0 - 35.0 mil
Side 1
1070 - 1220 microns
42.0 - 48.0 mil
Overall
Mechanical Properties Metric English Comments
Hardness, Shore A 50 - 60
50 - 60
Compound Property
Tensile Strength 6.21 - 7.58 MPa
900 - 1100 psi
Compound Property
Elongation at Break 450 - 550 %
450 - 550 %
Compound Property
Tear Strength >= 35.1 kN/m
>= 200 pli
Peel Strength >= 1.75 kN/m
>= 10.0 pli
Bond Strength
Compression Set <= 28 %
<= 28 %
after post cure
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Electrical Properties Metric English Comments
Dielectric Strength >= 15.7 kV/mm
>= 400 kV/in
Processing Properties Metric English Comments
Cure Time 30.0 min

@Temperature 177 °C
0.500 hour

@Temperature 350 °F
Recommended Cure Cycle
240 min

@Temperature 204 °C
4.00 hour

@Temperature 400 °F
after 30 minute ramp up cycle, Recommended Postcure Cycle
Shelf Life 3.00 Month

@Temperature 4.44 °C
3.00 Month

@Temperature 40.0 °F
From date of manufacture
Descriptive Properties Value Comments
Color Red
Total Product Weight (oz/yd2) 38.1 - 46.5
Uncoated Fabric Break Strength 250 lb/in
Fill Direction, Substrate Property
300 lb/in
Warp Direction, Substrate Property