Arlon 99410R015 0.015" Uncured Silicone Rubber with PTFE Coated Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 99410R015 0.015" Uncured Silicone Rubber with PTFE Coated Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Interleave: 0.001" FEPSide 1: Unsupported/Uncured Silicone RubberSubstrate: 0.003" PTFE coated FiberglassThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.

Physical Properties	Metric	English	Comments
Thickness	76.2 microns	3.00 mil	Substrate
	381 microns	15.0 mil	Rubber

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	50	50	Silicone Property
Tensile Strength	>= 4.83 MPa	>= 700 psi	Silicone Property
Elongation at Break	>= 250 %	>= 250 %	Silicone Property
Shear Modulus	<= 0.000689 GPa	<= 0.100 ksi
Shear Strength	2.76 MPa	400 psi	Lap

Thermal Properties	Metric	English
Thermal Conductivity	32.0 W/m-K	222 BTU-in/hr-ft²-°F
Maximum Service Temperature, Inert	232 °C	450 °F
Minimum Service Temperature, Air	-73.3 °C	-100 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	13.8 kV/mm	350 kV/in	tolerance - 5.25 KV minimum

Processing Properties	Metric	English	Comments
Cure Time	15.0 min @Temperature 121 °C	0.250 hour @Temperature 250 °F	Recommended Cure Cycle
Shelf Life	6.00 Month	6.00 Month

Descriptive Properties	Value	Comments
Color	Red
Thermal Impedance (°C/W)	1.3
Total Product Weight (oz/yd2)	17