Arlon 99580R010 0.010" (0.254 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier

Category Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 99580R010 0.010" (0.254 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction: Interleave: FEP FilmSide 1: Uncured Silicone Rubber Carrier: PTFE Coated FiberglassFlexible heater substrateAppearance: Red, High viscosity gum on release linersThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
Silicone Property; Arlon SQA-TMS-024
Thickness 25.4 microns
1.00 mil
Interleave
76.2 microns
3.00 mil
Carrier; Arlon SQA-TMS-003
254 microns
10.0 mil
Overall; Arlon SQA-TMS-003
254 microns
10.0 mil
Side 1; Arlon SQA-TMS-003
Mechanical Properties Metric English Comments
Hardness, Shore A 37
37
Silicone Property; ASTM D2240
Tensile Strength 6.55 MPa
950 psi
Silicone Property; ASTM D412
Elongation at Break 620 %
620 %
Silicone Property; ASTM D412
Tear Strength 26.3 kN/m
150 pli
Die B, Silicone Property; ASTM D624
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Flammability, UL94 HB

@Temperature 200 °C
HB

@Temperature 392 °F
per card E54153
Electrical Properties Metric English Comments
Dielectric Strength 47.87 kV/mm
1216 kV/in
ASTM D149
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Postcure Cycle
15.0 min

@Pressure 0.345 MPa,
Temperature 177 °C
0.250 hour

@Pressure 50.0 psi,
Temperature 350 °F
Recommended Cure Cycle
Shelf Life 6.00 Month

@Temperature 21.1 °C
6.00 Month

@Temperature 70.0 °F
From date of manufacture
Descriptive Properties Value Comments
Color Red
Total Product Weight (oz/yd2) 10.7
Arlon SQA-TMS-025