Arlon R38041X012 0.012" (0.305 mm) Uncured Fluorosilicone with Fiberglass Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon R38041X012 0.012" (0.305 mm) Uncured Fluorosilicone with Fiberglass Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction: Interleave 1: PolyethyleneSide 1: Uncured Silicone RubberSubstrate: Style 2116 FiberglassSide 2: Uncured Silicone Rubber Interleave 2: Polyethylene Appearance: Gray silicone gum and on fiberglass clothThis data represents typical values for the production material. The data should not be used to write, or in place of, material specificationsInformation provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Density 1.81 g/cc
0.0654 lb/in³
Fluorosilicone Property; Arlon SQA-TMS-024
Thickness 63.5 microns
2.50 mil
Interleave 1
63.5 microns
2.50 mil
Interleave 2
102 microns
4.00 mil
Side 1; Arlon SQA-TMS-003
102 microns
4.00 mil
Side 2; Arlon SQA-TMS-003
102 microns
4.00 mil
Substrate; Arlon SQA-TMS-003
305 microns
12.0 mil
Overall; Arlon SQA-TMS-003
Mechanical Properties Metric English Comments
Hardness, Shore A 65
65
Fluorosilicone Property; ASTM D2240
Tensile Strength 3.85 MPa
558 psi
Fluorosilicone Property; ASTM D412
Elongation at Break 82 %
82 %
Fluorosilicone Property; ASTM D412
Tear Strength 4.91 kN/m
28.0 pli
Die B, Silicone Property; ASTM D624
Peel Strength 0.193 kN/m
1.10 pli
Bond Strength; Arlon SQA-TMS-011
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Postcure Cycle
15.0 min

@Pressure 0.345 MPa,
Temperature 121 °C
0.250 hour

@Pressure 50.0 psi,
Temperature 250 °F
Recommended Cure Cycle
Shelf Life 6.00 Month

@Temperature 21.1 °C
6.00 Month

@Temperature 70.0 °F
From date of manufacture
Descriptive Properties Value Comments
Color Dark Gray
White
Substrate
Fuel Resistance 11.9
Fuel CM85 Resistance, ASTM D471
18.7
Fuel C Resistance, ASTM D471
6
Fuel A Resistance, ASTM D471
Total Product Weight (oz/yd2) 13.4
Arlon SQA-TMS-025, Product Property
81.4
Arlon SQA-TMS-025, Fluorosilicone Property