Arlon Thermabond® 99180T010 Silicone Rubber/Fiberglass Laminate

Category Polymer , Adhesive , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber
Manufacturer Arlon
Trade Name Thermabond®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon Thermabond® 99180T010 Silicone Rubber/Fiberglass Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Low outgassing, thermally conductive, electrically insulating, Thermabond®. Bonds with primer. Liner: 1 mil FEP; Product: uncured silicone rubber; Carrier: 3 mil PTFE coated fiberglass.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
silicone property; Arlon SQA-TMS-024
Thickness 254 microns
10.0 mil
overall; Arlon SQA-TMS-003
Mechanical Properties Metric English Comments
Hardness, Shore A 18
18
silicone property; ASTM D2240
Tensile Strength, Ultimate 6.89 MPa
1000 psi
silicone property; ASTM D412
Elongation at Break 950 %
950 %
silicone property; ASTM D412
Modulus of Elasticity 0.000517 GPa
0.0750 ksi
silicone property; Arlon SQA-TMS-008
Poissons Ratio 0.50
0.50
silicone property
Shear Strength 3.45 MPa
500 psi
silicone property; ASTM D1002
Thermal Properties Metric English Comments
CTE, linear 335 µm/m-°C

@Temperature 20.0 °C
186 µin/in-°F

@Temperature 68.0 °F
silicone property; ASTM E 831
Thermal Conductivity 0.900 W/m-K
6.25 BTU-in/hr-ft²-°F
silicone property; Arlon SQA-TMS-022
Maximum Service Temperature, Air 204 °C
400 °F
Minimum Service Temperature, Air -51.1 °C
-60.0 °F
Electrical Properties Metric English Comments
Dielectric Strength 39.4 kV/mm
1000 kV/in
ASTM D149
Processing Properties Metric English Comments
Cure Time 15.0 min

@Pressure 0.103 - 0.345 MPa,
Temperature 121 °C
0.250 hour

@Pressure 15.0 - 50.0 psi,
Temperature 250 °F
Shelf Life 6.00 Month

@Temperature 7.22 °C
6.00 Month

@Temperature 45.0 °F
Descriptive Properties Value Comments
Appearance Translucent