Armstrong A-661 Epoxy Adhesive

Category	Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	Armstrong Epoxy Adhesives; Resin Technology Group
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Armstrong A-661 Epoxy Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

A truly unique, two-component, room temperature curing thixotropic epoxy adhesive system, which exhibits good bond strength at service temperatures up to 400°F. Ideal for applications where resistance to high service temperatures is required, but where a room temperature cure is desirable.Information provided by Ellsworth Adhesives.

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	82	82
Tensile Strength, Ultimate	43.8 MPa	6350 psi	after optimum cure
Elongation at Break	2.5 %	2.5 %
Adhesive Bond Strength	34.8 MPa	5050 psi	Steel-Steel; after optimum cure
	17.2 MPa @Temperature -54.4 °C	2500 psi @Temperature -66.0 °F	Aluminum-Aluminum tensile shear
	22.8 MPa @Temperature 82.2 °C	3300 psi @Temperature 180 °F	Aluminum-Aluminum tensile shear
	26.9 MPa @Temperature 25.0 °C	3900 psi @Temperature 77.0 °F	Aluminum-Aluminum tensile shear

Thermal Properties	Metric	English
CTE, linear	35.0 µm/m-°C @Temperature 20.0 °C	19.4 µin/in-°F @Temperature 68.0 °F
Maximum Service Temperature, Air	204 °C	400 °F
Glass Transition Temp, Tg	115 °C	239 °F

Processing Properties	Metric	English	Comments
Processing Temperature	22.2 °C	72.0 °F
	149 °C	300 °F	Optimum cure is 10 min. @ 300°F
Pot Life	<= 180 min @Temperature 25.0 °C	<= 180 min @Temperature 77.0 °F	100 g

Descriptive Properties	Value	Comments
Color	Off White
Mix Ratio	4/1	By Weight