Asahi Kasei Leona® 14G25 25% Glass Filled Nylon 66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Asahi Kasei
Trade Name Leona®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Asahi Kasei Leona® 14G25 25% Glass Filled Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Enhanced strength and stiffness; with 25% GF. Superior heat aging resistance, fatigue resistance, and creep resistance.Applications:Mechanical and electrical parts, engine mounts and other under-the-hood automotive parts Information provided by Asahi Kasei
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
Dry; ASTM D792
Water Absorption 1.9 %
1.9 %
Wet
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
Dry; ASTM D2863
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
Dry; ASTM D2863
Mechanical Properties Metric English Comments
Hardness, Rockwell M 74
74
Wet; ASTM D785
96
96
Dry; ASTM D785
Hardness, Rockwell R 120
120
Dry; ASTM D785
Tensile Strength, Yield 110 MPa
16000 psi
Wet; ASTM D638
180 MPa
26100 psi
Dry; ASTM D638
Elongation at Break 3.0 %
3.0 %
Dry; ASTM D638
6.0 %
6.0 %
Wet; ASTM D638
Flexural Strength 175 MPa
25400 psi
Wet; ASTM D790
290 MPa
42100 psi
Dry; ASTM D790
Flexural Modulus 4.70 GPa
682 ksi
Wet; ASTM D790
8.10 GPa
1170 ksi
Dry; ASTM D790
Izod Impact, Notched 1.05 J/cm
1.97 ft-lb/in
Dry; ASTM D256
1.60 J/cm
3.00 ft-lb/in
Wet; ASTM D256
Taber Abrasion, mg/1000 Cycles 12
12
Wet; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear 30.0 µm/m-°C

@Temperature 20.0 °C
16.7 µin/in-°F

@Temperature 68.0 °F
Dry; ASTM D696
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
Dry
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Dry; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
Dry; ASTM D648
Flammability, UL94 HB
HB
Dry