Asahi Kasei Thermylene® P-10FG-2100 10% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Glass Fiber Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermylene® P-10FG-2100 10% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 92 | 92 | ASTM D785 |
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.34 GPa | 340 ksi | ASTM D638 |
| Flexural Strength | 68.9 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.74 J/cm | 7.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 54.0 µm/m-°C @Temperature 20.0 °C |
30.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | ASTM D648 |