Asahi Kasei Xyron® 540V Modified Polyphenylene Ether

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant
Manufacturer Asahi Kasei
Trade Name Xyron®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Asahi Kasei Xyron® 540V Modified Polyphenylene Ether.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame RetardantInformation provided by Asahi Kasei
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
23°C; ASTM D792
Moisture Absorption 0.100 %
0.100 %
23°C, 50% RH 24 hours; ASTM D570
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 64.0 MPa
9280 psi
23°C, 50% RH; ASTM D638
Elongation at Break 40 %
40 %
23°C, 50% RH; ASTM D638
Flexural Strength 98.0 MPa
14200 psi
23°C, 50% RH; ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
23°C, 50% RH; ASTM D790
Izod Impact, Notched 1.47 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
2.75 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature -30.0 - 60.0 °C
38.9 µin/in-°F

@Temperature -22.0 - 140 °F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
ASTM D648
Flammability, UL94 V-1

@Thickness 1.60 mm
V-1

@Thickness 0.0630 in
V-1

@Thickness 3.20 mm
V-1

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
50% RH; ASTM D257
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
50% RH; ASTM D257
Dielectric Constant 2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
50% RH; ASTM D150
2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
50% RH; ASTM D150
Dielectric Strength 29.0 kV/mm

@Thickness 2.00 mm
737 kV/in

@Thickness 0.0787 in
Short time; ASTM D149
Dissipation Factor 0.0030

@Frequency 60 Hz
0.0030

@Frequency 60 Hz
50% RH; ASTM D150
0.0040

@Frequency 1e+6 Hz
0.0040

@Frequency 1e+6 Hz
50% RH; ASTM D150
Arc Resistance 80 sec
80 sec
Tungsten; ASTM D495
Processing Properties Metric English Comments
Processing Temperature 240 - 290 °C
464 - 554 °F
Resin Temperature
Mold Temperature 50.0 - 80.0 °C
122 - 176 °F
Drying Temperature 90.0 - 100 °C
194 - 212 °F
Pre-drying Temperature
Dry Time 2 - 4 hour
2 - 4 hour