Ascend Performance Materials Vydyne® 41H BK03 Nylon 66, Impact Modified, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 41H BK03 Nylon 66, Impact Modified, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 41H BK03 is a general-purpose, impact-modified PA66 resin. Available in black, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne 41H BK03 was formulated to provide thermal endurance when used in applications in which continuous or extended high-temperature exposure is anticipated. Vydyne 41H BK03 is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline.Availability:Asia PacificEuropeNorth AmericaAdditive:Impact Modifier Features:Gasoline Resistance Good Abrasion ResistanceGood Chemical Resistance Good ProcessabilityHigh Impact ResistanceImpact ModifiedLow Temperature Impact Resistance Oil ResistantSolvent ResistantUses: Automotive ApplicationsConnectorsConsumer ApplicationsElectrical/Electronic ApplicationsFastenersGearsIndustrial Applications Appearance: BlackForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Water Absorption 1.0 %

@Time 86400 sec
1.0 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.1 %
2.1 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.018 cm/cm

@Diameter 2.00 mm
0.018 in/in

@Diameter 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.016 cm/cm

@Diameter 2.00 mm
0.016 in/in

@Diameter 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 39.0 MPa
5660 psi
ISO 527-2
Tensile Strength, Yield 35.0 MPa
5080 psi
ISO 527-2
Elongation at Break >= 180 %
>= 180 %
ISO 527-2
Tensile Modulus 1.39 GPa
202 ksi
ISO 527-2
Flexural Strength 17.0 MPa
2470 psi
ISO 178
Flexural Modulus 0.545 GPa
79.0 ksi
ISO 178
Izod Impact, Notched (ISO) 25.0 kJ/m²

@Temperature -40.0 °C
11.9 ft-lb/in²

@Temperature -40.0 °F
ISO 180
29.0 kJ/m²

@Temperature -30.0 °C
13.8 ft-lb/in²

@Temperature -22.0 °F
ISO 180
88.0 kJ/m²

@Temperature 23.0 °C
41.9 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 2.50 J/cm²

@Temperature -40.0 °C
11.9 ft-lb/in²

@Temperature -40.0 °F
ISO 179
2.50 J/cm²

@Temperature -30.0 °C
11.9 ft-lb/in²

@Temperature -22.0 °F
ISO 179
11.0 J/cm²

@Temperature 23.0 °C
52.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179