Material Notes:
Vydyne® 47 Nylon resins are general purpose polyamide, impact modified grades. They are available in natural, black and heat stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne 47H was formulated to provide thermal endurance when used in applications in which continuous or extended high temperature exposure is anticipated.Information provided by Ascend
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ISO 1183
Water Absorption 1.2 %
1.2 %
24 hrs; ISO 62
Linear Mold Shrinkage 0.018 cm/cm

@Thickness 2.00 mm
0.018 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.016 cm/cm

@Thickness 2.00 mm
0.016 in/in

@Thickness 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122
122
ISO 2039
Tensile Strength at Break 52.0 MPa
7540 psi
ISO 527
Tensile Strength, Yield 60.0 MPa
8700 psi
ISO 527
Elongation at Break 22 %
22 %
ISO 527
Tensile Modulus 2.78 GPa
403 ksi
ISO 527
Flexural Strength 70.0 MPa
10200 psi
ISO 178
Flexural Modulus 2.30 GPa
334 ksi
ISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature -40.0 °C
5.71 ft-lb/in²

@Temperature -40.0 °F
ISO 180
16.0 kJ/m²

@Temperature -30.0 °C
7.61 ft-lb/in²

@Temperature -22.0 °F
ISO 180
18.0 kJ/m²

@Temperature 23.0 °C
8.57 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact, Notched 1.10 J/cm²

@Temperature -40.0 °C
5.23 ft-lb/in²

@Temperature -40.0 °F
ISO 179
1.70 J/cm²

@Temperature -30.0 °C
8.09 ft-lb/in²

@Temperature -22.0 °F
ISO 179
1.90 J/cm²

@Temperature 23.0 °C
9.04 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 111 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
61.7 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359
CTE, linear, Transverse to Flow 136 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
75.6 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359
Melting Point 260 °C
500 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 185 °C
365 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 63.0 °C
145 °F
ISO 75
Flammability, UL94 HB

@Thickness 0.710 mm
HB

@Thickness 0.0280 in
Oxygen Index 21.7 %
21.7 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 6.90e+14 ohm-cm

@Thickness 1.00 mm
6.90e+14 ohm-cm

@Thickness 0.0394 in
ASTM D257-07
9.80e+14 ohm-cm

@Thickness 3.00 mm
9.80e+14 ohm-cm

@Thickness 0.118 in
ASTM D257-07
1.10e+15 ohm-cm

@Thickness 2.00 mm
1.10e+15 ohm-cm

@Thickness 0.0787 in
ASTM D257-07
Dielectric Strength 17.7 kV/mm

@Thickness 3.00 mm
450 kV/in

@Thickness 0.118 in
short time, 1/4" electrodes, 500 V/sec; ASTM D149-97a
24.4 kV/mm

@Thickness 2.00 mm
620 kV/in

@Thickness 0.0787 in
short time, 1/4" electrodes, 500 V/sec; ASTM D149-97a
29.9 kV/mm

@Thickness 1.00 mm
759 kV/in

@Thickness 0.0394 in
short time, 1/4" electrodes, 500 V/sec; ASTM D149-97a
Comparative Tracking Index 550 - 600 V

@Thickness 3.00 mm
550 - 600 V

@Thickness 0.118 in
IEC 60112