Ascend Performance Materials Vydyne® 47H BK0668 Nylon 66, Impact Modified, Heat Stabilized, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 47H BK0668 Nylon 66, Impact Modified, Heat Stabilized, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 47H BK0668 is a high-performance, medium-impact-modified, heat-stabilized grade of PA66 resin.Availability:Asia PacificEuropeNorth AmericaAdditive:Impact Modifier Features:Gasoline ResistanceGeneral Purpose Good Abrasion ResistanceGood Chemical Resistance Good ProcessabilityGood ToughnessHigh Impact ResistanceImpact ModifiedLow Temperature Impact Resistance Low Temperature ToughnessOil ResistantSolvent ResistantUses: Automotive ApplicationsConnectorsConsumer ApplicationsElectrical/Electronic ApplicationsFastenersGearsIndustrial Applications Appearance: BlackForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Water Absorption 1.2 %

@Time 86400 sec
 1.2 %

@Time 24.0 hour
 ISO 62
Moisture Absorption at Equilibrium 2.3 %
2.3 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.018 cm/cm

@Diameter 2.00 mm
 0.018 in/in

@Diameter 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.016 cm/cm

@Diameter 2.00 mm
 0.016 in/in

@Diameter 0.0787 in
 ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 52.0 MPa
7540 psi
ISO 527-2
Tensile Strength, Yield 60.0 MPa
8700 psi
ISO 527-2
Elongation at Break >= 22 %
>= 22 %
ISO 527-2
Tensile Modulus 2.78 GPa
403 ksi
ISO 527-2
Flexural Strength 70.0 MPa
10200 psi
ISO 178
Flexural Modulus 2.30 GPa
334 ksi
ISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature -40.0 °C
 5.71 ft-lb/in²

@Temperature -40.0 °F
 ISO 180
16.0 kJ/m²

@Temperature -30.0 °C
 7.61 ft-lb/in²

@Temperature -22.0 °F
 ISO 180
18.0 kJ/m²

@Temperature 23.0 °C
 8.57 ft-lb/in²

@Temperature 73.4 °F
 ISO 180
Charpy Impact Unnotched NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179/1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²

@Temperature -40.0 °C
 5.23 ft-lb/in²

@Temperature -40.0 °F
 ISO 179/1eA
1.70 J/cm²

@Temperature -30.0 °C
 8.09 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
1.90 J/cm²

@Temperature 23.0 °C
 9.04 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 11.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 6.11 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 14.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 7.78 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
Melting Point 260 °C
500 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 185 °C
365 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 63.0 °C
145 °F
Unannealed; ISO 75-2/A
UL RTI, Electrical 130 °C

@Thickness 0.750 mm
 266 °F

@Thickness 0.0295 in
 UL 746
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 UL 746
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 0.750 mm
 167 °F

@Thickness 0.0295 in
 UL 746
75.0 °C

@Thickness 1.50 mm
 167 °F

@Thickness 0.0591 in
 UL 746
75.0 °C

@Thickness 3.00 mm
 167 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 115 °C

@Thickness 0.750 mm
 239 °F

@Thickness 0.0295 in
 UL 746
115 °C

@Thickness 1.50 mm
 239 °F

@Thickness 0.0591 in
 UL 746
115 °C

@Thickness 3.00 mm
 239 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
Glow Wire Test 700 °C

@Thickness 0.750 mm
 1290 °F

@Thickness 0.0295 in
 Flammability Index; IEC 60695-2-12
700 °C

@Thickness 3.00 mm
 1290 °F

@Thickness 0.118 in
 Flammability Index; IEC 60695-2-12
725 °C

@Thickness 0.750 mm
 1340 °F

@Thickness 0.0295 in
 Ignition Temperature; IEC 60695-2-13
725 °C

@Thickness 3.00 mm
 1340 °F

@Thickness 0.118 in
 Ignition Temperature; IEC 60695-2-13
775 °C

@Thickness 1.50 mm
 1430 °F

@Thickness 0.0591 in
 Flammability Index; IEC 60695-2-12
800 °C

@Thickness 1.50 mm
 1470 °F

@Thickness 0.0591 in
 Ignition Temperature; IEC 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 ohm-cm

@Thickness 0.750 mm
 1.00e+11 ohm-cm

@Thickness 0.0295 in
 IEC 60093
Dielectric Strength 12.0 kV/mm

@Thickness 1.00 mm
 305 kV/in

@Thickness 0.0394 in
 IEC 60243
Arc Resistance 60 - 119 sec
60 - 119 sec
ASTM D495
Comparative Tracking Index 525 V

@Thickness 3.00 mm
 525 V

@Thickness 0.118 in
 IEC 60112
Hot Wire Ignition, HWI 7.0 - 14 sec

@Thickness 0.750 mm
 7.0 - 14 sec

@Thickness 0.0295 in
 UL 746
7.0 - 14 sec

@Thickness 1.50 mm
 7.0 - 14 sec

@Thickness 0.0591 in
 UL 746
15 - 29 sec

@Thickness 3.00 mm
 15 - 29 sec

@Thickness 0.118 in
 UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
 UL 746
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 UL 746
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 UL 746
High Voltage Arc-Tracking Rate, HVTR 25.5 - 80.0 mm/min
1.00 - 3.15 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 280 - 310 °C
536 - 590 °F
Middle Barrel Temperature 280 - 310 °C
536 - 590 °F
Front Barrel Temperature 280 - 310 °C
536 - 590 °F
Nozzle Temperature 280 - 310 °C
536 - 590 °F
Melt Temperature 285 - 305 °C
545 - 581 °F
Mold Temperature 65.0 - 95.0 °C
149 - 203 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Suggested Max Regrind 25 %