Ascend Performance Materials Vydyne® 66Z Nylon 66, DAM

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer	Ascend Performance Materials (formerly Solutia)
Trade Name	VYDYNE®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ascend Performance Materials Vydyne® 66Z Nylon 66, DAM.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Vydyne® 66Z is a high-viscosity PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 66Z resin offers high strength, rigidity and toughness over a broad range of demanding applications and good fluid resistance to a wide variety of chemicals, solvents and oils. Typical Applications/End Uses: Typical uses include packaging films, monofilaments, bristles, rods, tubing, sheet and extruded profiles.Availability:Asia PacificEuropeNorth America Features: Gasoline ResistanceGeneral Purpose Good Chemical ResistanceGood Melt StrengthGood ToughnessHigh RigidityHigh StrengthHigh ViscosityOil ResistantSolvent ResistantUses:Cast FilmFilmFood PackagingIndustrial ApplicationsMonofilamentsRodsSheetTubing Appearance: Natural ColorForms: PelletsProcessing Method: Extrusion and Injection MoldingInformation provided by Ascend Performance Materials.

Physical Properties	Metric	English	Comments
Density	1.14 g/cc	0.0412 lb/in³	ISO 1183
Water Absorption	8.5 % @Time 86400 sec	8.5 % @Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	2.5 %	2.5 %	50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.022 cm/cm @Diameter 2.00 mm	0.022 in/in @Diameter 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.021 cm/cm @Diameter 2.00 mm	0.021 in/in @Diameter 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	55.0 MPa	7980 psi	ISO 527-2
Tensile Strength, Yield	85.0 MPa	12300 psi	ISO 527-2
Elongation at Break	40 %	40 %	ISO 527-2
Elongation at Yield	5.0 %	5.0 %	ISO 527-2
Tensile Modulus	2.85 GPa	413 ksi	ISO 527-2
Flexural Strength	80.0 MPa	11600 psi	ISO 178
Flexural Modulus	2.40 GPa	348 ksi	ISO 178
Poissons Ratio	0.40	0.40	ISO 527-2
Izod Impact, Notched (ISO)	6.00 kJ/m² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	ISO 180
	7.00 kJ/m² @Temperature 23.0 °C	3.33 ft-lb/in² @Temperature 73.4 °F	ISO 180
Charpy Impact Unnotched	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.600 J/cm² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.700 J/cm² @Temperature 23.0 °C	3.33 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	10.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C	5.56 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F	ISO 11359-2
CTE, linear, Transverse to Flow	10.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C	5.56 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F	ISO 11359-2
Melting Point	260 °C	500 °F	ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi)	200 °C	392 °F	Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi)	65.0 °C	149 °F	Unannealed; ISO 75-2/A

Processing Properties	Metric	English	Comments
Zone 1	250 - 295 °C	482 - 563 °F
Zone 2	250 - 295 °C	482 - 563 °F
Zone 3	250 - 295 °C	482 - 563 °F
Zone 4	250 - 295 °C	482 - 563 °F
Zone 5	250 - 295 °C	482 - 563 °F
Die Temperature	270 - 295 °C	518 - 563 °F
Melt Temperature	270 - 295 °C	518 - 563 °F
Roll Temperature	20.0 - 80.0 °C	68.0 - 176 °F	Chill Roll Remperature

Descriptive Properties	Value	Comments
Blow Film Bath Temperature	20-80°C
Melt Pressure	3-17 MPa