Ascend Performance Materials Vydyne® R533 Nylon 66, 33% Glass Filled, Dry as Molded

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer	Ascend Performance Materials (formerly Solutia)
Trade Name	VYDYNE®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ascend Performance Materials Vydyne® R533 Nylon 66, 33% Glass Filled, Dry as Molded.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Vydyne® R533 is general-purpose, 33% glass-reinforced PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for good machine feed, flow, and mold release. Glass-reinforced Vydyne resins provide a higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals, including gasoline, hydraulic fluids and most solvents. Vydyne R533 has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption and part weight are key advantages of Vydyen glass-reinforced PA66 resins over aluminum and/or zinc die-cast parts. Typical Applications/End Uses: Vydyne R533 resin has been used for many under-the-hood automotive applications, motor housings for power tools and garden appliances. The resin has also been used in miscellaneous brackets, gears and clips, which require high rigidity and strength.Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 33% Filler by Weight Additive:Lubricant Features:Good FlowGood Mold Release High RigidityHigh StrengthLubricated Uses: Automotive Under the Hood GearsHousings Power/Other ToolsAppearance: Natural ColorForms: PelletsProcessing Method: Injection Molding

Physical Properties	Metric	English	Comments
Specific Gravity	1.40 g/cc	1.40 g/cc	ISO 1183
Water Absorption	0.80 % @Time 86400 sec	0.80 % @Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	1.7 %	1.7 %	50% RH; ISO 62
Linear Mold Shrinkage	0.0040 cm/cm @Thickness 2.00 mm	0.0040 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0090 cm/cm @Thickness 2.00 mm	0.0090 in/in @Thickness 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	205 MPa	29700 psi	ISO 527-2
Elongation at Break	3.0 %	3.0 %	ISO 527-2
Tensile Modulus	10.6 GPa	1540 ksi	ISO 527-2
Flexural Strength	290 MPa	42100 psi	ISO 178
Flexural Modulus	9.70 GPa	1410 ksi	ISO 178
Poissons Ratio	0.40	0.40	ISO 527-2
Izod Impact, Notched (ISO)	12.0 kJ/m²	5.71 ft-lb/in²	ISO 180
Charpy Impact Unnotched	7.00 J/cm² @Temperature -30.0 °C	33.3 ft-lb/in² @Temperature -22.0 °F	ISO 179
	8.00 J/cm² @Temperature 23.0 °C	38.1 ft-lb/in² @Temperature 73.4 °F	ISO 179
Charpy Impact, Notched	1.00 J/cm² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	ISO 179
	1.20 J/cm² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	2.10 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C	1.17 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F	ISO 11359-2
CTE, linear, Transverse to Flow	11.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C	6.11 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F	ISO 11359-2
Melting Point	260 °C	500 °F	ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi)	260 °C	500 °F	ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi)	250 °C	482 °F	ISO 75-2/A
UL RTI, Electrical	120 °C @Thickness 0.750 mm	248 °F @Thickness 0.0295 in	UL 746
	120 °C @Thickness 1.50 mm	248 °F @Thickness 0.0591 in	UL 746
	120 °C @Thickness 3.00 mm	248 °F @Thickness 0.118 in	UL 746
UL RTI, Mechanical with Impact	100 °C @Thickness 0.750 mm	212 °F @Thickness 0.0295 in	UL 746
	100 °C @Thickness 1.50 mm	212 °F @Thickness 0.0591 in	UL 746
	105 °C @Thickness 3.00 mm	221 °F @Thickness 0.118 in	UL 746
UL RTI, Mechanical without Impact	125 °C @Thickness 0.750 mm	257 °F @Thickness 0.0295 in	UL 746
	125 °C @Thickness 1.50 mm	257 °F @Thickness 0.0591 in	UL 746
	125 °C @Thickness 3.00 mm	257 °F @Thickness 0.118 in	UL 746
Flammability, UL94	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 ohm-cm @Thickness 3.00 mm	1.00e+14 ohm-cm @Thickness 0.118 in	IEC 60093
Dielectric Strength	20.0 kV/mm @Thickness 1.00 mm	508 kV/in @Thickness 0.0394 in	IEC 60243
Arc Resistance	120 - 179 sec @Thickness 3.00 mm	120 - 179 sec @Thickness 0.118 in	ASTM D495
Comparative Tracking Index	600 V @Thickness 3.00 mm	600 V @Thickness 0.118 in	IEC 60112
Hot Wire Ignition, HWI	7.0 - 15 sec @Thickness 0.750 mm	7.0 - 15 sec @Thickness 0.0295 in	UL 746
	7.0 - 15 sec @Thickness 1.50 mm	7.0 - 15 sec @Thickness 0.0591 in	UL 746
	7.0 - 15 sec @Thickness 3.00 mm	7.0 - 15 sec @Thickness 0.118 in	UL 746
High Amp Arc Ignition, HAI	>= 120 arcs @Thickness 0.710 mm	>= 120 arcs @Thickness 0.0280 in	UL 746
	>= 120 arcs @Thickness 1.50 mm	>= 120 arcs @Thickness 0.0591 in	UL 746
	>= 120 arcs @Thickness 3.00 mm	>= 120 arcs @Thickness 0.118 in	UL 746
High Voltage Arc-Tracking Rate, HVTR	10.1 - 25.4 mm/min	0.398 - 1.00 in/min

Processing Properties	Metric	English	Comments
Processing Temperature	285 - 305 °C	545 - 581 °F	Melt
Rear Barrel Temperature	280 - 310 °C	536 - 590 °F
Middle Barrel Temperature	280 - 310 °C	536 - 590 °F
Front Barrel Temperature	280 - 310 °C	536 - 590 °F
Nozzle Temperature	280 - 310 °C	536 - 590 °F
Mold Temperature	65.0 - 95.0 °C	149 - 203 °F
Drying Temperature	80.0 °C	176 °F
Dry Time	4.00 hour	4.00 hour

Descriptive Properties	Value	Comments
Suggested Max Regrind	50%