Azoty Tarnow™ TARFLEN SG-2 PTFE

Category Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Molded
Manufacturer Azoty Tarnow™ (Zaklady Azotowe)
Trade Name TARFLEN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azoty Tarnow™ TARFLEN SG-2 PTFE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Free-Flowing suspension powder for automated compression molding of complicated shapes and isostatic pressing.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Physical Properties Metric English Comments
Bulk Density 0.600 g/cc
0.0217 lb/in³
Density 2.15 g/cc
0.0777 lb/in³
ISO 1183
Particle Size 600 µm
600 µm
Average
Mechanical Properties Metric English Comments
Hardness, Shore D 58
58
ISO 868
Ball Indentation Hardness 34.0 MPa
4930 psi
ISO 2039-1
Tensile Strength, Yield 30.0 MPa
4350 psi
ISO 527
Elongation at Break 350 %
350 %
ISO 527
Izod Impact, Notched 1.30 J/cm
2.44 ft-lb/in
ISO 180
Charpy Impact, Notched 1.70 J/cm²
8.09 ft-lb/in²
1eA; ISO 179
Thermal Properties Metric English Comments
CTE, linear 125 µm/m-°C

@Temperature 20.0 °C
69.4 µin/in-°F

@Temperature 68.0 °F
ASTM E 831
Specific Heat Capacity 1.00 J/g-°C
0.239 BTU/lb-°F
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
Melting Point 327 °C
621 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.10e+18 ohm-cm
1.10e+18 ohm-cm
IEC 60093
Surface Resistance 4.50e+17 ohm
4.50e+17 ohm
IEC 60093
Dielectric Strength 72.0 kV/mm
1830 kV/in
IEC 60243-1
Dissipation Factor 0.00010
0.00010
IEC 60250
Arc Resistance 420 sec
420 sec
IEC 61621
Comparative Tracking Index 600 V
600 V
IEC 112
Processing Properties Metric English Comments
Processing Temperature 370 °C
698 °F
Molding
Back Pressure 20.0 - 35.0 MPa
2900 - 5080 psi
Molding Pressure