Azoty Tarnow™ Tarnamid® T-27 GF30 FRV0 Polyamide 6 - Flame Retarded, Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer Azoty Tarnow™ (Zaklady Azotowe)
Trade Name Tarnamid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azoty Tarnow™ Tarnamid® T-27 GF30 FRV0 Polyamide 6 - Flame Retarded, Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame retarded grades, flammability class V0, reinforced with 30% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning, low smoke density during exhibits.Tarnamid® has the following main properties:High mechanical strength, rigidity and hardnessHigh impact strengthHigh vibration damping capacityGood fatigue strengthVery good sliding properties, abrasion resistance, low coefficient of frictionHigh thermal resistance, admissible temperature of continuous operation from -60°C to +150°CHigh chemical resistance, particularly to organic solvents, oils, lubricants and fuelsConsiderable moisture absorption influencing mechanical and electrical propertiesSelf-extinguishing properties (fire retardant properties)Good electro-insulating propertiesGood optical properties, relatively good transparency of molded pieces with thickness below 3.2 mm made from natural Tarnamid® (not dyed and not compounded)Can be used for the production of goods coming into contact with food (grades fulfilling requirement of European Union Directive No 2002/72/EEC) with latest amendmentsInformation provided by Azoty Tarnow™.
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
ISO 1183
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ISO 294-4
Melt Flow 25 g/10 min

@Load 5.00 kg,
Temperature 275 °C
25 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 150 MPa

@Load 36.5 kg
21800 psi

@Load 80.5 lb
cond.; ISO 2039-1
240 MPa

@Load 36.5 kg
34800 psi

@Load 80.5 lb
dry; ISO 2039-1
Tensile Strength 105 MPa
15200 psi
cond.; ISO 527
150 MPa
21800 psi
dry; ISO 527
Elongation at Break 4.0 %
4.0 %
dry; ISO 527
5.5 %
5.5 %
cond.; ISO 527
Tensile Modulus 8.20 GPa
1190 ksi
cond.; ISO 527
10.0 GPa
1450 ksi
dry; ISO 527
Flexural Strength 135 MPa
19600 psi
cond.; ISO 178
220 MPa
31900 psi
dry; ISO 178
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
dry; ISO 179 1eU
8.00 J/cm²
38.1 ft-lb/in²
cond.; ISO 179 1eU
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
dry; ISO 179 1eA
1.20 J/cm²
5.71 ft-lb/in²
cond.; ISO 179 1eA
Thermal Properties Metric English Comments
Melting Point 221 °C
430 °F
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
cond.; ISO 75
200 °C
392 °F
dry; ISO 75
Vicat Softening Point 200 °C

@Load 5.10 kg
392 °F

@Load 11.2 lb
cond.; ISO 306
205 °C

@Load 5.10 kg
401 °F

@Load 11.2 lb
dry; ISO 306
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Glow Wire Test 960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
PN-EN-60695-2-12
Electrical Properties Metric English Comments
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 93
Dielectric Strength 28.0 kV/mm
711 kV/in
IEC 243-1
Comparative Tracking Index 525 V
525 V
IEC 112
Processing Properties Metric English Comments
Melt Temperature 230 - 290 °C
446 - 554 °F
Mold Temperature 60.0 - 120 °C
140 - 248 °F
80 - 90°C is recommended
Drying Temperature 75.0 - 100 °C

@Time 7200 - 14400 sec
167 - 212 °F

@Time 2.00 - 4.00 hour
Moisture Content <= 0.10 %
<= 0.10 %
Injection Pressure 80.0 - 130 MPa
11600 - 18900 psi
80 MPa is recommended