- BASF Luranyl® KR 2401 Polyphenylene Ether + Styrene-Butadiene Blend, Impact Grade
BASF Luranyl® KR 2401 Polyphenylene Ether + Styrene-Butadiene Blend, Impact Grade
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether + Styrene-Butadiene Blend , Styrene-Butadiene |
| Manufacturer | BASF |
| Trade Name | Luranyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Luranyl® KR 2401 Polyphenylene Ether + Styrene-Butadiene Blend, Impact Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Base grade with a balanced combination of impact strength and stiffness. Uses include: parts of vehicle interiors, air ducts and loudspeaker housings.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | |
| Water Absorption | 0.30 % | 0.30 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | |
| High Load Melt Index | 110 g/10 min @Load 21.6 kg, Temperature 250 °C |
110 g/10 min @Load 47.6 lb, Temperature 482 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | |
| Elongation at Break | 30 % | 30 % | |
| Elongation at Yield | 4.0 % | 4.0 % | |
| Tensile Modulus | 2.50 GPa | 363 ksi | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature 20.0 °C |
36.1 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 241 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | |
| Vicat Softening Point | 117 °C | 243 °F | |
| Flammability, UL94 | HB @Thickness 0.810 mm |
HB @Thickness 0.0319 in |
|
| Oxygen Index | 22 % | 22 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.6 @Frequency 100 Hz |
2.6 @Frequency 100 Hz |
|
| 2.6 @Frequency 1e+6 Hz |
2.6 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | |
| Dissipation Factor | 0.00050 @Frequency 1e+6 Hz |
0.00050 @Frequency 1e+6 Hz |
|
| Comparative Tracking Index | 300 V | 300 V |