BASF Luranyl® KR 2460/3 Polyphenylene Ether + Styrene-Butadiene Blend
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether + Styrene-Butadiene Blend , Styrene-Butadiene |
| Manufacturer | BASF |
| Trade Name | Luranyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Luranyl® KR 2460/3 Polyphenylene Ether + Styrene-Butadiene Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant grade with very high heat resistance; used for precision parts and where the material must withstand high injection temperatures (e.g. heater-fan impellers).Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | |
| Water Absorption | 0.40 % | 0.40 % | |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | |
| High Load Melt Index | 8.0 g/10 min @Load 21.6 kg, Temperature 250 °C |
8.0 g/10 min @Load 47.6 lb, Temperature 482 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | |
| Elongation at Break | 20 % | 20 % | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| Tensile Modulus | 2.80 GPa | 406 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 2.50 J/cm² | 11.9 ft-lb/in² | |
| 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature 20.0 °C |
36.1 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C | 315 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | |
| Vicat Softening Point | 160 °C | 320 °F | |
| Flammability, UL94 | V-0 @Thickness 3.10 mm |
V-0 @Thickness 0.122 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.8 @Frequency 1e+6 Hz |
2.8 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | |
| Dissipation Factor | 0.0050 @Frequency 1e+6 Hz |
0.0050 @Frequency 1e+6 Hz |
|
| Comparative Tracking Index | 250 V | 250 V |